Rapports scientifiques volume 12,
Scientific Reports volume 12, Article number: 7504 (2022) Cite this article
2269 Accesses
3 Citations
5 Altmetric
Metrics details
Failure in an epoxy polymer composite material is prone to initiate by the coalescence of microcracks in its polymer matrix. As such, matrix toughening via addition of a second phase as rigid or/and rubber nano/micro-particles is one of the most popular approaches to improve the fracture toughness across multiple scales in a polymer composite, which dissipates fracture energy via deformation mechanisms and microcracks arrest. Few studies have focused on tailorable and variable toughening, so-called ‘active toughening’, mainly suggesting thermally induced strains which offer slow and irreversible toughening due to polymer's poor thermal conductivity. The research presented in the current article has developed an instantaneous, reversible extrinsic strain field via remote electromagnetic radiation. Quantification of the extrinsic strain evolving in the composite with the microwave energy has been conducted using in-situ real-time fibre optic sensing. A theoretical constitutive equation correlating the exposure energy to micro-strains has been developed, with its solution validating the experimental data and describing their underlying physics. The research has utilised functionalised dielectric ferroelectric nanomaterials, barium titanate (BaTiO3), as a second phase dispersed in an epoxy matrix, able to introduce microscopic electro-strains to their surrounding rigid epoxy subjected to an external electric field (microwaves, herein), as result of their domain walls dipole displacements. Epoxy Araldite LY1564, a diglycidyl ether of bisphenol A associated with the curing agent Aradur 3487 were embedded with the BaTiO3 nanoparticles. The silane coupling agent for the nanoparticles’ surface functionalisation was 3-glycidoxypropyl trimethoxysilane (3-GPS). Hydrogen peroxide (H2O2, 30%) and acetic acid (C2H4O2, 99.9%) used as functionalisation aids, and the ethanol (C2H6O, 99.9%) used for BaTiO3 dispersion. Firstly, the crystal microstructure of the functionalised nanoparticles and the thermal and dielectric properties of the achieved epoxy composite materials have been characterised. It has been observed that the addition of the dielectric nanoparticles has a slight impact on the curing extent of the epoxy. Secondly, the surface-bonded fibre Bragg grating (FBG) sensors have been employed to investigate the real-time variation of strain and temperature in the epoxy composites exposed to microwaves at 2.45 GHz and at different exposure energy. The strains developed due to the in-situ exposure at composite, adhesive and their holding fixture material were evaluated using the FBG. The domain wall induced extrinsic strains were distinguished from the thermally induced strains, and found that the increasing exposure energy has an instantaneously increasing effect on the development of such strains. Post-exposure Raman spectra showed no residual field in the composite indicating no remnant strain field examined under microwave powers < 1000 W, thus suggesting a reversible strain introduction mechanism, i.e. the composite retaining its nominal properties post exposure. The dielectric composite development and quantifications presented in this article proposes a novel active toughening technology for high-performance composite applications in numerous sectors.
Among their high-performance engineering applications, fibre-reinforced polymer (FRP) composite materials have extensively been used with advantages of high specific strength and modulus, facile fabrication, considerable thermal resistance, and economic efficiency1. High-performance FRP composites have two major damage initiation modes when exposed to dynamic events; intra-laminar damage (e.g., matrix cracking, fibre fracture and fibre-matrix debonding) and inter-laminar damage (e.g., delamination)2,3,4. The intra-laminar damage is mainly dominated by matrix, fibre, and fibre-matrix interphase properties. However, it is challenging to tailor the properties of the fibre during composite's fabrication process.
To overcome these property-driven drawbacks, numerous researches have been carried out for property enhancement via modifying epoxy with the inclusion of various micro- and nano-fillers as a second phase, such as rubber tougheners5, silica particles6, carbon nanoparticles7,8, clay9 and fibre coating10. There are also various methods developed such as inter-penetrating network11, polymer plasticisation12, the addition of rubber13 and/or rigid inorganic particles like glass14, self-healing15 and volume dilation16. It has been observed that the rubber tougheners are the most effective ones, having substantial increase in the fracture toughness17 of a brittle epoxy by multiple orders of magnitude, though reduction in strength and stiffness are also observed18. An increase in fracture toughness of the glass/epoxy composites up to 82% is achieved by incorporating both core–shell rubber particles and silica nanoparticles19. It is also observed by many studies that a threshold exists and above which the particles tend to agglomerate and cause a degradation in mechanical properties20,18,19,23. The quality of particle/matrix interfacial bonding is another crucial factor that determines the mechanical properties of a modified epoxy matrix. Thus the application of coupling agents for surface treatment of particles is introduced to achieve a better interfacial bonding between particles and matrix24. Despite the excellent performance of particle-toughened epoxy composites, loss in elastic modulus, tensile strength, and glass transition temperature are also reported by other studies25. The addition of particles into the epoxy matrix often leads to a higher viscosity, and shear thinning behaviour26,27. Optimal uniform particles dispersion in epoxy resin is also a critical factor that requires to be achieved for a smooth load transfer between epoxy and fillers26. Although the modified epoxy with particles exhibits a promising future with excellent toughening performance, microcracks still formed in FRPs when subjected to varying or extreme operating conditions or during the manufacturing28, indicating an inherent level of uncertainty in the material's response that will require active toughness enhancement across the material. However, the toughness enhancement via second phase inclusion is only performed before service. When the epoxy matrix is exposed to varying mechanical loading during fabrication, storage, and service, microcracks are formed that are extremely difficult to detect and repair due to techniques limitation. Consequently, these internal micro-defects reduce the composite's performance, and their propagation may result in disastrous structural failure. Apart from such ‘one-off’ and irreversible toughening, a few studies focused on enabling the toughening effect by introducing an internal residual compressive stress field in the epoxy resin as a result of heating, offering ‘active’ and reversible toughening29. Such compression mechanism mainly relies upon the discrepancy in filler/matrix thermal expansion. However, the drawback of this approach is that the control of the toughening process is extremely challenging due to the poor thermal conductivity of polymer which slows down the material's response, mechanically. The toughening via volume dilation of embedded fillers is first proposed in a study by Ho Sung et al. It is achieved by pre-stressing the epoxy matrix via the expandable hollow microspheres under heating30. Thus far, there are no attempts made to date to investigate the strain behaviour of embedded fillers in rigid polymer composites under an electromagnetic field. Therefore, a study on radiation field induced strains has been investigated and presented, by incorporating ferroelectric crystals that demonstrates an electro-strain under an applied electric field.
Dielectric nanomaterials exhibit electric field induced strain which is attributed to intrinsic mechanisms from lattice deformation and extrinsic mechanisms due to domain wall (DW) movement31, extensively used as actuators and transducers. The inclusion of such material within a rigid epoxy FRP materials can impose a compressive stress field in its surrounding epoxy matrix when activated its DW movements by external electric field stimulation. As result of the DW movements, a microwave stimulation at GHz frequencies induces effective dipolar displacement (leading to intrinsic strains) to the nanomaterial's molecules that, at the interface with their surrounding rigid polymer, is converted to compressive mechanical strain. The hypothesis of this research was based upon suggesting that microcrack propagation during dynamic and impact events would be suppressed under such microwave induce d compressive stress–strain field, i.e. higher strain energy would be required to create new fracture surfaces, however the current article presents attempts on the quantification of the field induced strains. Therefore, the study focused on: 1—development of a modified epoxy with uniformly distributed dielectric nanomaterials that exhibit electro-strain, 2—in-situ quantification of its strain response under an electromagnetic field (e.g. microwave), and 3—establishment of a theoretical constitutive equation underpinning the correlation between the induced mechanical field and the microwave field.
To investigate the microstructural response of such dielectric nanomaterial embedded nanocomposite under an electromagnetic field, firstly, we developed a modified epoxy system with uniformly distributed barium titanate (BaTiO3) nanoparticles. Materials’ properties, functionalisation and fabrication methods developed in the research are described in "Materials and fabrication" section. Constitutive equations underpinning the multi-physics field induced strain and temperature have been provided in "Theoretical multi‑physics constitutive equations" section. With a second phase added to the epoxy system, the dielectric properties have been improved. Meanwhile, it also has effects on the curing extent of the epoxy system. Basic dielectric and cure state characterisation methods and their results are presented and described in "General material characterisations" section and "General material characterisations" section, respectively. To experimentally measure the perceivable strain effect induced by the stimulation of embedded BaTiO3 particles’ strains under microwave stimulation, fibre optic sensors utilising fibre Bragg grating (FBG) technique have been employed. The results of the in-situ measurements have been presented in In‑situ strain response under microwave at different power levels" section. Raman spectroscopy was employed to observe residual internal stresses post microwave exposure. Its results are presented and discussed in "Raman characterisation" section. The theoretical solution from the newly established constitutive expressions have been presented, where their ability to underpin the experimental data have been assessed.
BaTiO3 like other ferroelectric materials exhibit spontaneous polarisation at its polar phase that could be switched by applying an external electric field32,33, containing crystals having a net permanent polarisation which is the vector sum of all the dipole moments in a unit cell34,35, due to the absence of a centre of symmetry. When an electric field is applied, while the strength of the field increases, the polarisation increases and reaches a saturation state where all dipoles are aligned with the field direction. When the external field is removed, the polarisation may not return back to zero, i.e. displaying a remnant polarisation \(P_{r}\)36.
BaTiO3 domain wall is characterised by the angle of polarisation axes between two adjacent domains, such as 180° and 90° domain walls37, existing in a tetragonal phase of BaTiO338. Generally speaking, 180° domain walls are only responsive under electric fields while the other non-180° domain walls are responsive under both electric and mechanical stress fields37. Therefore, the DW configuration of BaTiO3 is defined by its own structure, and it changes by dipole displacements under an electric field or mechanical loading39. When an electric field is applied to the BaTiO3 crystals with a perovskite structure, three main representative deformations contribute to its mechanical strain response40, the intrinsic strain is induced by its electrostriction and piezoelectric effects while the extrinsic strain is attributed to the domain wall movement in the polydomain materials as presented in Fig. 1.
Schematic diagram of the extrinsic strain and intrinsic strain that contributes to macroscopic strain in a tetragonal BaTiO3 crystal embedded in epoxy (red, green and blue arrows represent electric field induced intrinsic strain, extrinsic strain and macroscopic strain, respectively).
The 90° domain switching in BaTiO3 introduces a large electro-strain due to the exchange of two different crystallographic axes, and the field induced strain is one or two orders of magnitude larger than the linear electro-strain of piezoelectric materials. After the removal of the electric field, the domain structure cannot be restored to its original form due to lack of energy and remnant polarisation in each domain. Therefore, the 90° domain switching is theoretically a one-time process41. Due to the lack of driving force to restore the original domain configuration after removing the field, the domain wall movement is irreversible and consequently the macroscopic strain42. The 90° domains in BaTiO3 crystals are capable of introducing a large strain that is attributed to the crystallographic axes exchange under alternating electric field42. However, it is difficult to distinguish the contributions from intrinsic and extrinsic (domain wall movement) contributions and conventionally, the single-domain crystals are considered to be only affected by the intrinsic properties while the contributions of the extrinsic domain wall movement are investigated in the polydomain crystals, as observed in37. Therefore, in this research, polydomain BaTiO3 nanoparticles is employed to achieve the field-induced strain effect.
The mechanism of the material and microwave interaction is particularly complex and it involves the orientation of dipoles, free-to-move electrons, domain wall movement and electron spins, which are activated by the electric and/or magnetic field components43. The essence of the interaction between the dielectric material and the electromagnetic field is energy transformation at the molecular level. Therefore, the dielectric properties of a material, which is measured as the complex permittivity quantifies the ability of a dielectric material to absorb and store electrical potential energy when exposed to a microwave field44. The complex permittivity that represents the microwave-material interactions are expressed by:
where \(\varepsilon^{\prime}\) is the real parts of the permittivity that indicating the ability to store microwave energy of the material while \(\varepsilon ^{\prime\prime}\) is the imaginary part of the permittivity that indicating the ability to dissipate the microwave energy44. The dielectric loss tangent is expressed by:
The loss tangent is the measure of the material to convert absorbed energy into other forms of energy such as heat45. The dipoles in an alternating electric field will reorient themselves to align with the new field direction. However, this process cannot occur instantaneously due to inherent non-zero inertia, and thus some time is required to fulfil the reorientation of the dipoles. At microwave frequencies, dipole polarisation is assumed to be the most dominant one for energy transfer at the molecular level.
In this section, the theoretical analysis of the strain field induced in BaTiO3 nanoparticles embedded epoxy under microwave exposure is established. Firstly, the theory of dynamic elastic response of tetragonal BaTiO3 nanoparticles under alternating electric field at the microwave exposure is presented and discussed46. The displacement of the DWs is utilised as the eigenstrain for the estimation of the strain field in the BaTiO3-epoxy nanocomposite. A novel approach based on the principle of virtual work of the equivalent eigenstrain is incorporated in the calculation of the inhomogeneous inclusion47. Based on this approach, a theoretical framework of microwave activated dynamic elastic response of the nanocomposite has been established. Finally, the non-uniform distribution of the microwave field and the interaction with the samples have been incorporated in the framework.
The 90° DW movement is considered to have the major contribution to the extrinsic field-induced strain. Therefore, the tetragonal BaTiO3 nanoparticle is assumed to be formed by several multi-domain crystallites that contain a laminar 90° domain structure. A conceptual schematic of a crystallite is shown in Fig. 2. \(\Delta l\) is the displacement of domain walls under microwave radiation; \(d\) is domain size and \(g\) (identified in the figure) is the particulate size, i.e. in our case and grain size in polycrystal. The domain wall movement in such crystallite is assumed to be not affected by that in other crystallites.
Schematic illustration of a spherical nanoparticle (simplified as a crystallite) with a laminar 90° domain structure with spontaneous polarisation \({{\varvec{P}}}_{0}\) and domain size \({\varvec{d}}\), recreated from48.
Before the application of the microwave field, it is assumed that the DWs are in an equilibrium state, and all the domains are of an identical size, dielectric properties and elastic properties. Therefore, the interactions between adjacent domains are not included as it is assumed negligible compared with other factors as suggested in a previous study49. Moreover, the internal electric and mechanical fields are assumed to be negligible, hence no forces acting on the DWs prior to the microwave exposure50. When the microwave field is applied, the interactions with the magnetic component are negligible since BaTiO3 is non-ferrite. The alternating electric component of the microwave field is assumed to be homogenous across the whole nanoparticle in this research. It is assumed that the spontaneous polarisations in the 90° domains re-orient themselves with the direction of an applied alternating electric field. Consequently, a driving force \(f_{A} \left( t \right)\) as the function of time is introduced on the DWs that enables the DW motion due to polarisation change51. The displacement of the DW movement is denoted as \(\Delta l\) in Fig. 2. Due to the BaTiO3 ferroelectricity, such movement introduces an internal electric field \(E\) in the nanoparticle due to the change in the polarisation direction. As a result, the internal stress field is also no longer negligible due to the newly developed internal electric field and DW movement from its equilibrium position. An additional force \(f_{I}\) on the DWs is developed subsequently due to the change in the internal electric and stress fields from zero state. Due to the displacements in DWs, the electric dipole moment \(\Delta p\) induced by the internal electric field, and the elastic dipole moments \(\Delta v\) induced by the internal mechanical stress field are given by52:
where \(P_{0}\) is the spontaneous polarisation, and \(S_{0}\) is the spontaneous deformation. The correlation between \(\Delta l\) and the dipole moments is assumed to be linear, and their internal energy \(W_{electric}\) under the internal electric field \(E\), and \(W_{elastic}\) under mechanical stress field \(T_{13}\) are:
where \(E\) is the internal electric field, and \(T_{13}\) is the internal mechanical stress \(T_{ij}\) (\(i\), \(j\) = 1, 2, 3) as illustrated in a cartesian coordinate system (\(x_{1}\), \(x_{2}\), \(x_{3}\)) in Fig. 2.
The expression for the DW motion is51:
By the derivation of Eqs. (5) and (6), the force \(f_{I}\) due to the internal fields per unit area \(k\Delta l\) is obtained from
where \(k\) is the force constant per unit DW area, and \(A_{DW}\) is the area of the DW. The displacements for the DWs from their equilibrium state under the microwave field are assumed to have the same magnitude, \(\left| {\Delta l\left( t \right)} \right|\). The force \(f_{I}\) per unit DW area at a random point \(r\), and time \(t\) can then be expressed by Eq. (8):
The DWs motion is then described by the Newton's second law of motion:
where \(m\) is the mass of a DW per unit area, \(\overline{f}_{I} \left( t \right)\) is the mean value of the DWs driven force \(f_{I}\) from the internal fields, \(f_{A} \left( t \right)\) is the aforementioned exerted force on the DWs by the applied microwave field. The \(\overline{f}_{I} \left( t \right)\) is then calculated by averaging the \(f_{I} \left( {r,t} \right)\) over the summation of the DWs surfaces (\(d\Sigma\)) in a nanoparticle, as presented below46.
The DW displacements induced internal electric field \(E\left( {r,t} \right)\) and internal mechanical field \(T_{13} \left( {r, t} \right)\) in Eq. (11) must firstly be calculated prior to the \(\overline{f}_{I} \left( t \right)\) calculation. The internal electric field was evaluated in a quasi-static approximation for a given microwave field, and \(E\left( {r,t} \right)\) is considered to be proportional to the DW displacement \(\Delta l \left( t \right)\). The interal mechanical stress field \(T_{ij}\) was considered as a dynamic problem as the DW motions lag behind the 2.45 GHz microwave frequency46. In this study, only the extrinsic effect, i.e. the DW motions, is considered as they are commonly accepted to be the primary contributor to the electro-strain compared with the intrinsic effect such as piezoelectric effect and electrostriction.
To obtain the value of the internal mechanical stress field, the change of the spontaneous deformation \(S_{0}\) introduced by the DW displacements in Eq. (11) was calculated, thus the \(\Delta S_{13}^{0} \left( {r,t} \right)\) and \(\Delta S_{31}^{0} \left( {r,t} \right)\) were approximated by46:
where \(w\) is the thickness of a 90° DW, \({V}_{DW}\) is the volume of DWs without an applied microwave field, and \(\delta \left({V}_{DW}\right)\) is the Dirac delta function for \({V}_{DW}\).
The thickness \(w\) is approx. 100 Å, much smaller compared with the domain width \(d\) and the particle size48, therefore, Eq. (12) was simplified to Eq. (13)46.
where \(\Sigma\) represents the midplanes of DWs when \(\Delta l=0\), \({\delta }_{3}\left(\Sigma \right)\) is the Dirac delta function of the \(\Sigma\) with a unit normal directed along the \({x}_{3}\) axis53.
The electric component of the oscillating microwave field is a sinusoidal function of time and the DW displacement \(\Delta l\left(t\right)\) is written as
where \(\Delta {l}_{m}\) is the maximum displacement of the DWs under the microwave field. The nanoparticle is assumed to be a homogeneous and isotropic dielectric medium, and the internal electric field \(E\left(r,t\right)\) is proportional to \(\Delta l\left(t\right)\),
where \({\varepsilon }_{0}\) is the permittivity of the free space (\({\varepsilon }_{0}=8.8542\times {10}^{-12}\) F/m), \(d\) is the width of the DW, and \({h}_{e}\left(r\right)\) are approximated as46:
where \({\epsilon }_{11}\) is first component of the dielectric permittivity tensor \({\epsilon }_{ij}\) (\(i,j=\mathrm{1,2},3\)) that represents the dielectric permittivity of the crystallite as illustrated in Fig. 2, and \({\varepsilon }^{*}\) is the dielectric permittivity of the nanoparticle. The force \({\overline{f} }_{I}\) was then calculated with the internal mechanical stress field \({T}_{13}\left(r, t\right)\), and the internal electric field \(E\left(r,t\right)\) from Eqs. (15) and (16). The field-induced force \({f}_{A}\) is due to the effective electric field in the \({x}_{1}\) direction of the applied microwave field as illustrated in Fig. 2. The electric field component \({E}_{A1}\) is a function of time as follows:
where \({E}_{m}\) is the amplitude of the electric component of the microwave field, and \(\mathrm{\varnothing }\) is the phase lag of the DW motion relative to the oscillatory microwave field. Equation (17) is then substituted into Eq. (8) with the second part equalling zero as \({f}_{A}\left(t\right)\) is only introduced by an electric field:
Finally Eqs. (11), (15), and (18) are substituted into Eq. (10), giving:
where \({\overline{h} }_{s} ,{\overline{h} }_{c},\mathrm\,{and}\,{\overline{h} }_{e}\) are the average of \({h}_{s}\left(r\right),{h}_{c}\left(r\right) and\, {h}_{e}\left(r\right)\) over DW surface \(\Sigma\), evaluated using the expressions outlined in46. From Eq. (19), it could be seen that the DW displacement \(\Delta {l}_{m}\) is correlated with the properties and strength of the electric component of the microwave field \({E}_{m}\) and the dielectric permittivity of the nanoparticle. The value of the DW displacement \(\Delta {l}_{m} \left(\omega \right)\) could be obtained by numerical computations of the \({\overline{h} }_{s}\left(\omega \right)\) and \({\overline{h} }_{c}\left(\omega \right)\).
To get an approximate estimate, a further simplification was made that the nanoparticles are sufficiently small to be considered as a multi-domain single crystal, namely a crystallite. Therefore, the crystallite as illustrated in Fig. 2 could be considered as a single BaTiO3 nanoparticle without any adjacent crystallite, and hence no corresponding internal electric and stress field. Consequently, Eq. (10) is simplified to:
It is assumed that the DW movement under the oscillatory microwave field is a simple harmonic motion with a driven force of \({f}_{A}\left(t\right)\). Neglecting the lag in the dipoles reorientation, the DW motion becomes in phase with the oscillating field. The driving force at the maximum electric field strength \({f}_{m}\) is then obtained by:
and the amplitude \(\Delta {l}_{m}\):
where \(Y\) is the young's modulus of the BaTiO3 nanoparticle and \(d\) is the domain width where the area of the domain is approximated to be \({d}^{2}\).
Eshelby's inclusion approach has been employed in this study to compute the effective stress field within an epoxy matrix with the embedded BaTiO3 nanoparticle. General Eshelby's inclusion problem involves ellipsoidal inclusions in an infinite linear elastic medium54,55. Firstly, equations based on the elastic theory to solve the eigenstrain of Elshelby's inclusion have been utilised, in which the total strain of infinitesimal deformations is expressed as:
where \({e}_{ij}\) is the elastic strain, and \(\varepsilon_{ij}^{*}\) is the eigenstrain. The compatibility condition of total strain \(\varepsilon_{ij}\) is expressed in terms of displacement \({u}_{i}\), i.e.
The stress \({\sigma }_{ij}\) is then expressed by the Hooke's Law,
where \({C}_{ijkl}\) is the effective stiffness tensor, \({C}_{ijkl}={C}_{ijlk}\) and \({C}_{ijkl}{u}_{k,l}={C}_{ijkl}{u}_{l,k}\). In the region where \({\varepsilon }_{kl}^{*}=0\), Eq. (25) is re-arranged to:
The inversed Eq. (25) is then expressed by:
where \({S}_{ijkl}\) is the compliance tensor that has the same symmetries as the stiffness tensor. The equation of equilibrium is then expressed as follows:
where \({f}_{i}\) is the body force, and the boundary condition is:
where \({n}_{j}\) is the outward unit normal vector to the boundary. The corresponding stress and strain field of a homogeneous inclusion in an infinite medium could be obtained using Green's function method with the profile of the inclusion56: The Eshelby inclusion's problem is applied as illustrated in Fig. 3. It is assumed that the inclusion has a dynamic deformation of the eigenstrain \(\varepsilon (t)\) as a function of time under the microwave field. A fictitious load \(T\) is applied to the inclusion to maintain the original shape. The inclusion is then placed back into the hole within the infinite epoxy matrix with the original shape and size. After removing the applied \(T\), the inclusion exerts a traction force \(F\) on the matrix, which equals \(-T\).
Schematic diagram of Eshelby's inclusion utilised in our analysis.
It is assumed that the inclusion is in ellipsoids shape and have identical elastic properties with the matrix. Furthermore, the eigenstrain in the inclusion is assumed uniform. Therefore, the inhomogeneous inclusion of embedded BaTiO3 nanoparticles has been solved by transforming the inhomogeneous inclusion into a homogenous inclusion. The nanoparticle with residual strain embedded within the epoxy was transformed into a homogenous inclusion problem with a distribution of equivalent eigenstrain.
The transformation illustrated in Fig. 4 was based on the principle of virtual work47. Firstly, the inclusions in both inhomogeneous and homogeneous cases in Fig. 4 are imaginarily cut-sectioned from the matrix, and the virtual works are expressed in Eq. (30), over the Ω region of the inhomogeneous problem, and Eq. (31) over the Ω0 region of the virtual homogeneous problem.
where \(\delta {u}_{i}\) is the virtual displacement, \(\delta \varepsilon_{ij}\) is the virtual strain, \({f}_{i}\) is the body force, \({T}_{i}\) is the traction force on the boundary, and \(\sigma_{ij}\) is the stress field in the nanoparticle. Equation (31) minus Eq. (30) gives:
Schematic diagram of the principle of equivalent eigenstrain of transforming inhomogeneous problem to a virtual homogeneous problem.
As the stress state in both conditions are identical, therefore, \({{f}_{i}=f}_{i}^{*}\), and \({T}_{i}={T}_{i}^{*}\). The \(\delta \varepsilon_{ij}\) can take any arbitrary value, and Eq. (32) is then expressed as follows:
From the stress expression in Eq. (25), the stress state is obtained as Eq. (34) over Ω, and Eq. (35) over Ω0:
where \({C}_{ijkl}\) and \(C_{ijkl}^{*}\) are the elastic constant tensors of the homogeneous and inhomogeneous inclusion, respectively, \({\varepsilon }_{kl}\) is the total strain, \({\varepsilon }_{kl}^{*}\) is the real residual strain in the inhomogeneous Ω, and \({\varepsilon }_{kl}^{0}\) is the equivalent eigenstrain in the homogeneous Ω0. Since \({{f}_{i}=f}_{i}^{*}\) and \({T}_{i}={T}_{i}^{*}\), the deformation of the nanoparticle in epoxy in Ω is equivalent to that of the virtual homogeneous inclusion in Ω0 by incorporating an equivalent eigenstrain \({\varepsilon }_{kl}^{0}\). The substitution of Eq. (33) with Eqs. (34) and (35) gives:
The equivalent eigenstrain in Ω0 is then expressed by:
Therefore, with the equivalent eigenstrain \({\varepsilon }_{ij}^{0}\), the stress and strain field in the nanoparticle over Ω could be calculated using Green's function method as follows47,56, accounting for the displacement field for a 3D inclusion:
where \({G}_{ij,l}\left({\varvec{X}}-{{\varvec{X}}}^{\boldsymbol{^{\prime}}}\right)\) is the Green's function, and
The strain field is then obtained from Eq. (38), i.e.
The total strain in Eq. (37) is then expressed equivalent to the eigenstrain \({\varepsilon }_{ij}^{0}\) given by Eq. (40), which gives:
Therefore, the corresponding deformation field in the inclusion and the matrix can be calculated using Green's function method with the equivalent eigenstrain \({\varepsilon }_{ij}^{0}\). As illustrated in Fig. 5, a BaTiO3 nanoparticle is embedded in the epoxy matrix, assumed to be in full bonding with the epoxy (i.e. no disbond or interfacial defect) and the epoxy is assumed to be infinite. The BaTiO3 nanoparticle and the epoxy are assumed to be isotropic. A nominal eigenstrain \({\varepsilon }_{ij}^{*}\), due to the DW movement is prescribed as shown in the figure. It is assumed that the eigenstrain is the collective displacements of all the domains that may exhibit different polarisation in all possible directions.
Schematic view of a BaTiO3 nanoparticle with radius (\({\varvec{r}}\)) embedded in the epoxy matrix with eigenstrain (\(\Delta {{\varvec{l}}}_{{\varvec{m}}}\)).
The nominal eigenstrain is denoted as \({\varepsilon }_{ij}^{*}\):
The anisotropic elastic constants of isotropic materials are \({C}_{ijkl}\), and \({C}_{ijkl}^{*}\) for Epoxy and BaTiO3 respectively:
where \(\lambda \left({\lambda }^{*}\right)\) and \({\mu (\mu }^{*})\) are Lame constants57, \(v\) is the Poisson ratio, and \({\delta }_{ij}\) is the Kronecker delta. Inserting Eqs. (43) and (44) into Eq. (37):
The equivalent eigenstrain \({\varepsilon }_{kl}^{0}\) and total strain can then be re-written as \({\varepsilon }_{kl}\):
where \(\varepsilon\) is a function of \({\varepsilon }_{0}\)56:
Therefore, Eq. (47) is:
And the equivalent eigenstrain \(\varepsilon_{0}\) is solved by Eq. (50):
Therefore, the strain \({\varepsilon }_{kl}\) in the epoxy is expressed by:
The major interaction between the dielectric material and the microwave field is the polarisation of the dipoles, i.e. under an oscillatory microwave field, the dipoles re-orient themselves with the external electric field component of the microwave field. Therefore, the BaTiO3 nanoparticles interact with the electric field component of the microwave field, and the magnetic field effect is considered negligible. The main contribution of microwave power loss in the multi-domain BaTiO3 nanoparticles originates from the piezoelectric domain wall movement58. Compared with the BaTiO3 nanoparticles, the dielectric loss tangent of epoxy represents the ability to dissipate the absorbed energy is relatively smaller (in the range of 10−3 to 10−4)59. The mobility of the polar segments of polymer decreased significantly when the frequency reaches the GHz range60. Therefore, the dielectric loss in BaTiO3-Epoxy nanocomposites observed at a higher frequency (e.g. microwave at 2.45 GHz) is mainly attributed to the BaTiO3 nanoparticles.
The behaviour of the electric and magnetic components of the microwave field is governed by Maxwell's equations coupled with boundary conditions61.
where \(\mathbf{H}\) and \(\mathbf{E}\) are the varying magnetic (A/m) and electric field strength (V/m), respectively, \(\omega\) is the angular frequency (rad/s), \(\varepsilon\) is the complex relative permittivity, \(\mu\) is the complex relative permeability, and \(\rho\) is the charge density. The first two equations, so-called Ampere's law and Faraday's law, correlate the changes in the electric or magnetic field. The last two equations are Gauss's laws, which represents the net magnetic flux out of a region. It must be zero while the net electric flux out of a region is related to the charge density within the region62. The power absorbed by the material in the microwave field is dependent on many factors such as shape, size, and location of the material. For a relatively thin material that fully penetrated by the microwave field, the power dissipated \(P\) (W/m3) as heat in the material under microwave field is expressed based on Maxwell's Equation as follows63:
where the first term \(\mu_{0} \mu^{\prime\prime}H_{rms}^{2}\) describes the dissipation of power due to magnetic field and can be neglected for a non-ferrite material, e.g. BaTiO3, \(\omega =2\pi f\), \(f\) is the frequency of the applied microwave field (= 2.45 GHz), \({\varepsilon }_{0}\) is the dielectric permittivity of the free space, \(\varepsilon^{\prime \prime }\) represents the imaginary part of the complex dielectric permittivity, and \({E}_{rms}\) is the root-mean-square value of the local electric field strength (V/m). Therefore, Eq. (57) is simplified to:
However, the explicit evaluation of the absorbed power by the material inside the oven cavity is difficult to obtain due to the non-uniformity of the microwave distribution, and hence a varying electric field strength. The power absorbed by the material \({P}_{absorb}\), is expressed as follows:
where \({P}_{input}\) is the input power from the magnetron, \({P}_{reflected}\) is the power reflected and attenuated, and \({P}_{oven}\) is the power absorbed by the cavity wall, waveguide, and magnetron. The increased temperature due to microwave heating also has a significant impact on the dielectric properties of the material, which in turn affect the degree of interaction of the nanocomposite with the microwave field. In previous studies, an empirical approach has been proposed to estimate the absorbed power. It is assumed that the amount of microwave energy absorbed by the material/field interaction is converted into heat during the exposure, and is expressed as follows64,65:
where \(m\) is the mass of the material, \(C\) is the specific heat capacity of the material, \(\Delta T\) is the temperature change, \(V\) is the volume of the material, and \(t\) is the microwave exposure time.
The energy transferred into the material is also significantly determined by the depth up to which the microwave field travels into it. The degree of microwave penetration in the material is defined by a factor, Penetration depth (\({d}_{p}\))66,67, which is the distance between the surface of the material and the place inside the material where the magnitude of the field strength drops to \({e}^{-1}\) (36.8%) of that at the surface. The penetration depth \({d}_{p}\) neglecting the effects from the magnetic field for a non-ferrite material is expressed as follows65:
where \(c\) is the velocity of light, \({\varepsilon }^{^{\prime}}\) is the real part of the complex dielectric permittivity, and \(\mathrm{tan}\delta\) is the tangent loss of the material, \(\tan \delta = \varepsilon \prime \prime /\varepsilon \prime\). Generally speaking, the microwave power decays more quickly in lossy materials with higher \(\mathrm{tan}\delta\) due to energy dissipation hence a lower penetration depth.
From Maxwell's equation, it is noted that the energy of the microwave field is proportional to the square of the amplitude, which represents the maximum strength of its electric and magnetic components. For a continuous sinusoidal microwave field in the air of an empty cavity, the average intensity \(I\) is the power carried by the microwave field per unit area, and is expressed as follows68:
where \({E}_{m}\) is the maximum electric field strength, and the root-mean-square value of the electric field is:
Equations 62 and 63 above could only be used to calculate the electric field strength in an empty oven. When a sample is placed in the multimode microwave oven (our case), the electromagnetic field is considered to be a superposition of multiple plane waves penetrate the material from different directions. Regardless of the differences in each mode, the superposition of all the waves could be assumed to have an approximately uniform and constant distribution pattern in the material within the localised region69. Assumptions are made that the absorbed microwave energy is converted to heating in the material with neglected surface heat loss, thermal diffusion, and energy absorbed by the oven (e.g. magnetron and cavity wall). Therefore, the energy absorbed by the material is corresponding to the temperature rise of the material, and it is expressed by re-arranging Eq. (60):
It should be noted that the internal electric field is only localised in the material and is different from that in the surrounding cavity. Under the same assumptions that the material is surrounded by a uniform microwave field, incident microwaves are mostly transmitted and absorbed by the material while some are reflected. It is also assumed no reflected wave at the interface. An expression is presented as follows70:
where \(V\) is the volume of the material, \(\rho\) is the density of the materials, \(c\) is the phase velocity of the microwave (\(3\times {10}^{8}\) m/s)71, \(A\) is the surface area, \(\xi\) is the absorption coefficient that represents the fraction of the absorbed power that generates heat, and \(\Gamma\) is the transmission coefficient. Solving the equation, the time-averaged strength of the external electric field \({E}_{rms, external}\) obtained by:
The power absorption coefficient \(\xi\) is expressed as follows72:
where \({P}_{0}\) is the incident power at the surface, and \(a\) is the thickness of the BaTiO3-epoxy sample. The transmission coefficient, \(\Gamma\), is the energy fluxes per unit time and unit area at the interface. It is assumed that the microwave incident is normal to the material surface as the energy flux comes from all directions within the cavity, and the transmission coefficient \(\Gamma\) is simplified as71:
where \({n}_{1}\) and \({n}_{2}\) are the refraction index of air and the material, respectively. The above equations are employed to theoretically obtain an estimate of the average and peak electric field strengths of the incident microwave with a given cavity size. Subsequently, the absorbed microwave power by the nanocomposite has been estimated.
The epoxy used in this study was Araldite LY1564, a diglycidyl ether of bisphenol A (DGEBA) and the curing agent was Aradur 3487, an amine hardener, supplied by Huntsman, UK. This epoxy resin system has relatively low viscosity and high flexibility mainly for aerospace and industrial structural composites parts. The coupling agent for surface functionalisation selected in this study was 3-glycidoxypropyl trimethoxysilane (3-GPS) supplied by Sigma-Aldrich, US. Hydrogen peroxide (H2O2, 30%) and acetic acid (C2H4O2, 99.9%) used as functionalisation aids were supplied by Sigma-Aldrich, US, and the ethanol (C2H6O, 99.9%) used for BaTiO3 dispersion by Fisher Scientific International, Inc., UK. BaTiO3 powders were supplied from Nanostructure & Amorphous Materials Inc., US. The general properties of the powders measured by the manufacture, detailed in Table 1, below73. All the chemicals except BaTiO3 powders were used as received without further treatment.
The phase composition of BaTiO3 powders has been confirmed by X-Ray diffraction (XRD) using a Siemens D5005 X-Ray Diffractometer with Cu-Kα radiation (wavelength λ of 1.54 Å, at 40 kV and 30 mA). The scanning speed was 0.5°/s in the range of 20° to 90°. The peaks analysis was performed by data analysis software Origin using a Lorentzian curve fit function. Figure 6 shows a well-defined perovskite structure of BaTiO3 without a noticeable second phase. The split peaks between 44°and 46° of the 2θ angle correspond to reflections (002) and (200) confirms the tetragonal phase of BaTiO374.
X-ray diffraction patterns of purchased BaTiO3 powders. The inset shows the split peaks of (002) and (200) indicating the tetragonal phase.
The BaTiO3 powders were prepared using combustion method, therefore, firstly they were pre-treated in H2O2 for hydroxylation process to add hydroxyl group (-OH) to the surface75: 10 g BaTiO3 nanoparticles were added into a 230 mL solution of H2O2 in a round bottom flask. The mixture was then sonicated in an ultrasonic bath for 30 min and then refluxed at the boiling temperature of 30% H2O2 solution at 108 °C76 at 100 rpm using a mechanical stirrer for 6 h to facilitate the process by heating without losing H2O2. The nanoparticles were retrieved by centrifuging the resulting solution at 4500 rpm for 15 min, and washed three times with deionized water. The achieved BaTiO3 nanoparticles were dried in an oven at 80 °C for 24 h. The reflux and particle retrieving processes were similar as in the surface functionalisation with 3-GPS as shown in Fig. 7. 3-GPS was then applied to BaTiO3 nanoparticles to improve the processability and filler dispersion in nanocomposites; the solution of 1 wt.% of 3-GPS with respect to BaTiO3 was prepared. 150 mL aqueous solution of ethanol and deionized water (9:1) was firstly mixed in a beaker. Adding the acetic acid drops using a pipette and stir vigorously after each drop until the pH value of 3.5–4 measured by a METTLER TOLEDO pH meter was reached, stirred vigorously again for 3 min to form a clear solution. The low pH values of the solution facilitate the silane functionalisation process77. After the addition of the 0.1 g 3-GPS solution to the acidified solution using a pipette, the mixture was left in an ultrasonic bath for 30 min to form a homogenous solution. 10 g hydroxylated BaTiO3 powders was then added to the silane solution, and mixed under ultrasonic bath for 10 min for better filler wetting. Finally, the mixture was refluxed at the boiling temperature of ethanol, 78 °C78, at 100 rpm using a mechanical stirrer for 6 h using a silicone oil bath over a hotplate. After refluxing, the BaTiO3 was washed three times with deionized water and retrieved using centrifugation at 4500 rpm. The silane treated BaTiO3 (Si-BaTiO3) powders were dried at 110 °C for 24 h to avoid any condensation of silanol groups at the surface. In the end, the powders were crushed in a mortar and pestle for the nanocomposites preparation. The size distribution of Si-BaTiO3 particles was analysed in its epoxy nanocomposite form. The surface functionalisation didn't significantly affect the particle size as shown in the SEM images and it is approximately 200 nm (discussed in "Scanning electron microscope (SEM)." section).
Schematic diagram of the functionalisation process of BaTiO3 with 3-GPS.
The silane-treated powders were characterised by Thermogravimetric analysis (TGA) and Fourier transform infrared (FTIR) spectrometry to confirm the presence of the functional group in the following sections.
FTIR is performed to detect the silane functional groups on the modified BaTiO3 powders in transmission mode using a Jasco FT/IR-6200 in the range of 400–4000 cm−1 with a resolution of 2 cm−1 at room temperature. The FTIR spectra of Si-BaTiO3 and untreated powders are presented in Fig. 8. The peaks at 1437 cm−1 and 1630 cm−1 are due to the small trace of BaCO3, and physically absorbed water on BaTiO3 powders from the combustion fabrication process according to the manufacturer79. The bands at 3200–3700 cm−1 are attributed to hydroxyl groups OH (from Si–OH group) stretching vibrations. The bands between 850 and 1250 cm−1 are representations of Si–O, Si–O–C2H5, and Si–O vibrations. These new peaks confirm that the silane group are successfully grafted onto the surface of BaTiO3 powders80.
FTIR spectra of Si-BaTiO3 (black) and untreated (red) BaTiO3 powders.
The amount of organic silane group grafted onto the surface of BaTiO3 powder was obtained by TGA using a TA instruments Q-500 at a rate of 20 °C/min under a dry nitrogen gas flow rate of 100 ml/min to 700 °C, shown in Fig. 9 for untreated and Si-BaTiO3 powders. The weight loss percentage indicated as the lowest point of the green line is 0.35% of untreated BaTiO3 and 1.2% for treated. Therefore, the amount of 3-GPS grafted onto the BaTiO3 surface was calculated to be approx. 0.85%, which is close to the previously designed 1% in the surface functionalisation process. The weight curve of 3-GPS treated BaTiO3 powders showed three well-defined degradations as labelled in the figure. Based on the FTIR results, the absorbed water is removed between 50 to 150 °C, (1) and (2) in the figure. The degradation step from 240 to 450 °C represents the free hydroxyl groups (–OH) and/or silane molecules that remained on the surface, labelled as (3). The pyrolysis of surface silane compounds was observed at around 565 °C, labelled as (4)79,81. The increase in weight between 650 and 700 °C is only observed in the untreated powder and it is attributed to the impurities in the as-received powder (supplied from US Research Nanomaterials Inc) reacting with nitrogen.
TGA curves of untreated and Si-BaTiO3 powders. Green lines indicate the weight percentage of the powders versus temperature, and blue lines the rate of change of the weight percentage versus temperature.
The epoxy resin nanosuspension with 1, 5, 10, 15 wt.% Si-BaTiO3 nanoparticles and 5, 10, 15 wt.% untreated BaTiO3 nanoparticles were prepared as follows: Firstly, the weighed amount of BaTiO3 powders was added to ethanol and sonicated with an ice water bath for 2 min with a 10 s pulse to form a homogenous solution. Then a weighed amount of epoxy and the previous mixed solution were blended in a beaker using a mechanical stirrer at 300 rpm and 80 °C overnight under the fume hood to gradually remove the ethanol without precipitation of the particles. The mixture was weighed before and after the previous step to ensure the complete removal of ethanol. The curing agent was then added to the mixture with a weight ratio recommended by the company and stirred for a further 3 min. Finally, the mixture was placed in the vacuum oven at 30 °C for 1 h to remove bubbles at 29 inHg and achieve complete removal of ethanol. The whole mixture was poured into a mould made of two pieces of glass clamped with a 3 mm silicone gasket in-between, as shown in Fig. 10. A uniform thickness of each sample was achieved with the assistance of this type of glass mould. They were then cured in the oven for 8 h at 80 °C as prescribed by the manufacturer, then cooled down to room temperature. The final samples were of size 160 × 140 × 3 mm3, and cut to different sizes using a precision cut-off machine BRILLANT 220.
Glass mould used for nanocomposite fabrication and the cured nanocomposite samples.
The morphological characterisation of the nanocomposites, post cure, with different weight loading between 0 wt.% and 15 wt.% were carried out using a field emission scanning electron microscope TESCAN Vega 3. A thin layer of gold is coated to each sample before testing to enable better conductivity. The thermal characterisation of the cured nanocomposites was studied using a differential scanning calorimeter (DSC Q200, TA Instruments). The DSC measurements were performed in a nitrogen flow (50 mL/min). Samples 5 × 3 × 1 mm3 were prepared using a Buehler ISOMAT low speed saw. The samples were first heated from 40 to 220 °C at 20 °C/min. The measured DSC curves of all epoxy nanocomposites presented a distinct exotherm peak. Thereafter, the second run at a heating rate of 20 °C/min was conducted up to 220 °C after cooling down from the first scan. The glass-transition temperature (\({T}_{g}\)) was determined using the inflection-point method following the IS/DIS 11,357-2. A tangent was drawn at the point of inflection in the DSC spectra from the second run, and the \({T}_{g}\) was the midpoint between onset and end-set of the drawn tangent.
The complex relative permittivity and permeability of the neat epoxy and the nanocomposites at different weight loading were measured with increasing frequency from 0.25 to 4.50 GHz at a 0.25 step increment using a vector network analyser (VNA) with microstrip methods82. Flat plates samples of size 50 × 50 × 3 mm3 were prepared as substrates for conductive lines as shown in Fig. 11. They were then attached to a ground metal plate at the bottom. The dielectric constants of the samples were then measured using the VNA. The resonant approach can provide a more accurate values of the dielectric properties compared with the transmission line method. However, the resonant methods could only measure the dielectric properties at a single frequency instead of measuring in the frequency range83.
Schematic illustration of the layout of sample for microstrip line methods.
The microwave field was selected to be the external stimulator as BaTiO3 exhibit a peak in a dielectric loss at the microwave frequency range. Most importantly, the design of the experiment becomes more feasible with remote stimulation from the microwave field owing to the spacious cavity. The mechanical strain evolution in the nanocomposite was investigated under a microwave field within a temperature-controlled microwave cavity Panasonic NN-SF464MBPQ running at 2.45 GHz and cavity size of 354 × 338 × 230 mm3. In contrast with the conventional one, this oven, equipped with inverter technology, has a circuit board that replaces the transformer, hence the output power can be adjusted linearly by varying the pulse width to ensure a more precise and continuous microwave exposure84. The unique flat-bed design of this model is equipped with a stationary ceramic plate that allowed more space to place the sample and its holder.
The strain field introduced by the BaTiO3 nanoparticles to the surrounding epoxy, activated by microwave field, was studied by real-time strain measurements on the surface of the nanocomposite samples with the incorporation of Fibre optic sensors utilising fibre Bragg gratings (FBG) technique. The sensors were placed apart in equal distance from one another within a 90 mm straight line. This is theoretically aligned with the microwave's half wavelength (~ 60 mm) as also was experimentally observed during real-time temperature measurements. The sensors were located to ensure overlapping with at least three nodes and antinodes of the microwave cycle. The FBG sensors were fabricated by a periodic intense laser light applied onto the core of an optic fibre. The laser light exposure introduced a permanent increase in the refractive index of the fibre's core and a fixed modulation was created subsequently. Each FBG was approx. five mm long with a grating period of one micron. Two arrays with three FBGs for each sample were fabricated. FBG arrays were then adhesively bonded to the surface of two geometrically identical 135 × 10 × 3 mm3 samples made of Si-BaTiO3 epoxy nanocomposites. The strain array was bonded to the surface by adhesives at the FBG regions while the temperature array is firstly packaged into a capillary glass tube, and then bonded parallel to the strain array. The arrays were placed at the same location with the same distance in-between. The strain experienced by the samples was transferred to the FBG sensors, and the measurements were also affected by the temperature. Therefore, the temperature array only measured the temperature change, and compensated the strain measurements accordingly.
A preliminary test via a FLIR One Pro LT Thermal Camera was carried out to inspect the temperature change in different samples under different microwave power levels. Samples were placed at a designed location as shown in Fig. 12. The exposure time was then carefully selected based on the heating profiles of each sample to control the temperature of samples well below \({T}_{g}\) during the exposure to avoid any interference in strain measurements from the post-cure shrinkage. The sample was clamped on one end by a designed sample holder made of polytetrafluoroethylene (PTFE) to ensure minimum interaction with the microwave field owing to its extremely low dielectric loss. The size and location of the load inside the cavity were two primary factors that affect the microwave field distribution84. To control the microwave field distribution, the sample and the holder were placed at the designed location shown in the figure, for all tests. The power level of 100 W and 440 W were initially selected to avoid temperature surges in samples within a short period of time. Exposure time was set to be 650 s for 100 W and 148 s for 440 W to limit the temperature below \({T}_{g}\) (80 °C) based on the preliminary results obtained by the thermal camera.
Schematic illustration of the sample of epoxy nanocomposite with BaTiO3 on the PTFE holder in the microwave oven with surface bonded FBG arrays connected to an interrogator.
Neat epoxy, BaTiO3 nanoparticles, and adhesive used for bonding FBGs possess different thermal expansion coefficients (CTE) and microwave heating patterns. Microwave field interaction with the neat epoxy and adhesive have been investigated, thereafter. Two arrays with five FBGs of five mm long and one micron grating period were fabricated for each test. First, the adhesive response under microwave radiation was studied by two arrays of FBGs adhesively bonded to the surface of a PTFE block. It is assumed that measured strain and temperature change are solely due to the microwave heating of adhesive as PTFE has neglectable thermal response (temperature rise) under the microwave. The PTFE block is placed in the microwave oven at the designed location to locate the first FBG sensor on the left end at the same location as the one in the previous exposure on the nanocomposites. The tests have been performed under 100 W for 650 s and 440 W for 110 s. Data was recorded on the interrogator 10 s prior to the microwave exposure for each run to ensure no data is missing after the microwave starts. The effect of neat epoxy with the FBG sensors bonded to its surface was investigated as a controlled group to the test of 15 wt.% nanocomposites at 10 W for 600 s and 440 W for 60 s. Neat epoxy sample geometrically identical with 15 wt.% nanocomposites in the nanocomposite's exposure test was placed in the designed location with surface-bonded arrays of FBGs. The whole measurements from adhesive and the neat epoxy were compared with the results from the previously performed test on the nanocomposites for better distinguishing the BaTiO3-epoxy nanocomposite's response to the microwave exposure.
Raman characterisation was carried out to investigate residual stress, any indication of remnant strain field or crystal structure change in BaTiO3 nanoparticles embedded epoxy post microwave exposure. Neat epoxy samples and 15 wt.% BaTiO3 epoxy nanocomposites with the identical geometric dimension of 135 × 10 × 3 mm3 were characterised before and after 440 W microwave radiation of 110 s. The Raman spectra were obtained using a Raman spectroscope Horiba Scientific LabRAM HR with a 514 nm excitation wavelength laser for all samples.
A silane coupling agent 3-GPS was introduced to modify the BaTiO3 particles in this work to achieve a finer dispersion in epoxy. To examine its effectiveness, the dispersion and distribution of the nanoparticles at epoxy with different loadings have been characterised using the SEM. Different levels of aggregation events due to increased weight fraction of particles and enhancement of distribution due to surface functionalisation were present:
Figure 13a–f presents the SEM images of the fractured cross-section of the silane functionalised and non-functionalised BaTiO3 epoxy composites at various wt.%. It is shown that the nanoparticles are uniformly dispersed with the aid of surface functionalisation. As shown in Fig. 13a, the silane-treated particles are of the similar size of 200 nm as pristine BaTiO3 particles. There is no apparent aggregation of Si-BaTiO3 particles until small-scale clusters become visible in Fig. 13c,d when the loading of BaTiO3 reaches 10 wt.% and over, due to nanofillers agglomeration as circled in Fig. 13c,d. Overall, the majority of the Si-BaTiO3 particles were finely dispersed compared with the untreated ones. Figure 13e,f show images of the composites with 15 wt.% non-functionalised BaTiO3 particles at different magnification. In contrast with the functionalised BaTiO3 at the same weight loading 15 wt.% shown in Fig. 13d, the 15 wt.% untreated BaTiO3 exhibit severe agglomeration to form large clusters that have left large-scaled lamellar structures. The efficacy of the silane functional group is in good agreement with works conducted by others85,83,87.
SEM images of fracture cross of epoxy nanocomposites with BaTiO3 at different weight loading, (a)–(d) images of 1 wt.%, 5 wt.%, 10 wt.% and 15 wt.% Si-BaTiO3/Epoxy nanocomposite samples. (e) and (f) 15 wt.% untreated-BaTiO3-epoxy nanocomposite at lower (670x) and higher (6620x) magnification.
The DSC was conducted to examine the effect on curing extent and \({T}_{g}\) of cured epoxy nanocomposites with varying weight fractions of Si-treated and untreated BaTiO3 nanoparticles.
Figure 14 shows the DSC spectra of the neat epoxy and nanocomposites at various BaTiO3 content as an attempt to provide a comparative analysis between the variation of Tg in the different multi-material systems. As observed from the insets, the DSC spectra of epoxy nanocomposites exhibit insignificant bumps denoted as exothermic peaks representing the post-curing process due to the impeded curing by the existence of BaTiO3 nanoparticles, i.e. indicating the nanocomposite material is well cured with the current weight loadings of the BaTiO3 particles. The \({T}_{g}\) transition for the coloured lines that represent nanocomposites are shifted slightly to lower temperatures compared with the black line of neat epoxy which is evidence of reduced \({T}_{g}\) as the nanoparticles hindered the curing process of the epoxy resin88. Furthermore, the weak endothermic peaks that emerge on the spectra represent the relief of the stress introduced during processing and handling or the thermal history. The thermal history and residual stress were removed from the first run of heating and the samples were post-cured during the first DSC analysis up to 200 °C. The true \({T}_{g}\) of each cured nanocomposite sample was calculated based on the DSC spectra of a second run under the same condition.
DSC spectra of neat epoxy and nanocomposites with 10 wt.% and 15 wt.% of untreated BaTiO3 (pink and green) and Si-BaTiO3 (red and blue). Weak endothermic peak around Tg and weak exothermic peak from 160 to 220 °C are identified.
Figure 15a presents the DSC spectra of a second heating scan for each epoxy nanocomposite with functionalised BaTiO3 after cooling down from the 220 °C previous runs. The glass temperatures per nanocomposite category have been identified in Fig. 16. It can be observed that epoxy nanocomposites are well cured without any perceptible exothermal peak. The red and black lines are drawn as a demonstration of \({T}_{g}\) variation along with the weight fraction of the nanofiller. The red line shows a gradual increase of \({T}_{g}\) with the increasing Si-BaTiO3 content. The \({T}_{g}\) has increased up to 90 °C compared with that of the neat epoxy, 87 °C, as shown in Fig. 17. The increased \({T}_{g}\) represents that more energy is needed from higher temperatures to complete the glass transition process, which indicates that the movement of polymer chains is inhibited by the functionalised BaTiO3 nanoparticles due to improved interfacial bonding. However, by adding the non-functionalised BaTiO3, the \({T}_{g}\) shows a remarkable drop at 5 wt.% at the beginning as marked by a black line in Fig. 15b. When the weight loading reaches 10 wt.%, the \({T}_{g}\) shows an increment surge from 81 to 84 °C. The \({T}_{g}\) of the nanocomposites reaches 89 °C at 15 wt.%. The untreated particles at 5 wt.% have a negative effect on the Tg by obstructing the formation of the cross-linking structure of epoxy due to particle agglomeration as shown previously in the SEM images. However, the addition of the nanoparticles can enhance the mobility of the polymer chain by introducing increased free volume at the filler-matrix interface89. For the uncured pure epoxy resin, the mobility of the polymer segments decreases and Tg increases with the temperature rise during the curing process. When the Tg finally approaches the curing temperature and becomes higher, the curing process ceases due to the lack of mobility of the segments. The free volume created by introducing more untreated nanoparticles increases the mobility of the segments during curing, and hence favours the curing process and higher Tg.
(a) DSC spectra of the neat epoxy (black) and Si-BaTiO3-Epoxy nanocomposite samples at 5 wt.% (Red), 10 wt.% (Blue), and 15 wt.% (Pink), (b) Tg temperature as a function of weight loading of Si-BaTiO3 (Red) and untreated BaTiO3 (Black) of the epoxy nanocomposites samples.
Glass transition temperatures of silane treated and untreated BaTiO3-Epoxy nanocomposites.
Dielectric measurements (a) real permittivity \({\varvec{\varepsilon}}\boldsymbol{^{\prime}}\), (b) loss tangent \({\varvec{t}}{\varvec{a}}{\varvec{n}}({\varvec{\delta}})\) from 0 to 4.5 GHz at room temperature of neat epoxy and BaTiO3-Epoxy nanocomposites at different weight loading.
The microwave dielectric properties of the epoxy nanocomposites were investigated from 0.25 to 4.50 GHz at a 0.25 step increment using a VNA PNA-X N5245A via a stripline technique at room temperature. The real permittivity \({\varepsilon }^{^{\prime}}\) and dielectric loss tangent \(\mathrm{tan}\delta\) calculated from Eq. (2) at room temperature are shown in Fig. 17.
The \({\varepsilon }^{^{\prime}}\) of all samples over the measured frequency range have slight reduction trends with increasing frequency due to the dipoles in the material that cannot follow the speed of the alternating field and reorient themselves with the field direction89. Compared with neat epoxy, the inclusion of Si-BaTiO3 nanoparticles at 10 wt.% and 15 wt.% give a perceptible rise to the value of \({\varepsilon }^{^{\prime}}\) through the frequency range, which are similar results as reported in other studies90,88,92. In the meantime, the 1 wt.% and non-treated 10 wt.% BaTiO3/Epoxy samples present similar values of \({\varepsilon }^{^{\prime}}\) with the neat epoxy due to little amount of BaTiO3 of 1 wt.% and aggregations of unfunctionalized 10 wt.%92. The silane treated samples have higher values in \({\varepsilon }^{^{\prime}}\) due to a more uniform dispersion of BaTiO3 nanoparticles90,91,93. However, there aren't huge differences between the values of \({\varepsilon }^{^{\prime}}\) at 10 wt.% and 15 wt.%. As discussed formerly, the ferroelectricity character of tetragonal BaTiO3 enables a spontaneous polarisation that can be reversed by an applied field94. Therefore the \({\varepsilon }^{^{\prime}}\) of epoxy is enhanced due to the addition of BaTiO3 nanoparticles, which agrees with the findings from other researches90,91,93,95. Generally speaking, a substantial increase in the dielectric properties of modified epoxy is only achieved by a generous amount of BaTiO3 content as high as 90 wt.%96. The blue line that represents the dielectric response of 5 wt.% silane-treated BaTiO3 epoxy nanocomposites, exhibiting clearly a significantly lower value of real permittivity \({\varepsilon }^{^{\prime}}\) below the neat epoxy's. This drastic decline in the value of \({\varepsilon }^{^{\prime}}\) is attributed to the testing errors from airgaps that were identified due to the uncertainties associated with handling the samples, between the sample and conductive line97 while was not observed in the other samples. Figure 17b illustrates that the loss tangent in all samples increases with increasing frequency. On the contrary with the real permittivity, the loss tangent has slightly decreased with adding BaTiO3 powders except from 1 wt.% content. The loss tangent of a composite system has contributions from dipole orientation, conduction loss and interfacial polarisation98. Silane treatment of the BaTiO3 powders introduce a reduction of the concentration of ionizable hydroxyl groups (-OH) on the BaTiO3 surface and hinders the mobility of the charge carriers on the surface. The lowered conduction loss could be the primary reason for lowered loss tangent80.
Labelling for strain and temperature FBG arrays is illustrated in Fig. 18. Field-induced strains in the nanocomposites with 15 wt.% BaTiO3 (the highest wt.% examined) has been investigated within a microwave exposure at 100 W and 440 W (Figs. 19 and 20, respectively) in the three specimens which exhibited nearly similar trends and magnitude (one data presented in the figures in the interests of clarity). The evolution of strain and temperature have been measured in situ by the two arrays; one array measures the strain while the other one measures the temperature. Sudden drastic fluctuations and absent data presented in FigS. 19 and 20 are due to Bragg wavelengths moving into adjacent spectral windows that were set up on the sensor interrogator.
Schematic illustration of surface-bonded FBG arrays measuring in-situ temperature and strain.
Strain and temperature change measurements of 15 wt.% silane-treated BaTiO3-Epoxy samples under 100 W for 600 s.
Strain and temperature change measurements of 15 wt.% silane-treated BaTiO3-Epoxy samples under 440 W for 148 s.
The strain and temperature data exhibit a general increasing trend with the exposure. They drop gradually, immediately, after the microwave stopped. The temperature appeared to be higher at both ends of the specimen (sensor 1 and 3, located left and right respectively) compared to the middle (sensor 2), which is in accordance with the ‘hot spot’ theory due to microwave nonuniformity as illustrated in Fig. 21. Sensors 1 and 3 data also follows more similar temperature increasing trend (magnitude and rate). The microwave oven cavity is designed to be a multimode resonant cavity, similar to a closed waveguide. The microwaves generated by the magnetron are reflected back and forth by the metal walls inside the cavity and eventually forms standing waves throughout the cavity's volume as illustrated in Fig. 2199. The illustration is accompanied by a thermal image captured from the sample under the microwave, showing the approximate locations of the nodes and anti-nodes. As seen, the anti-nodes (hot spots) are located at or surrounding the sensors. Under microwave exposure, the distance between the area with higher temperature (antinodes) and the cold spot with lower temperature (nodes) is a quarter of the wavelength, which is approximately 31 mm100. The sensors have been positioned equal distances apart, and accordingly, they fell in different temperature zones under the standing waves, identified schematically in the figure (assuming that the far-left edge of the sample represents a node).
Schematic illustration of (above) the location of FBGs on the sa mple surface, and (below) standing waves formed in a microwave oven showing hot spots (antinodes) and cold spots (nodes).
The strain measured from a FBG sensor is derived from the change in the wavelength of reflected ultraviolet light due to grating period change. The change with strain and temperature is expressed by101:
where \(\Delta \lambda\) is wavelength shift, \({\lambda }_{0}\) is the base wavelength, \(k=1-p\), \(p\) is the photo-elastic coefficient, \(p\) =0.22, \(\varepsilon\) is the strain due to both mechanical and thermal factors, \(\Delta T\) is the temperature change, and \({\alpha }_{\delta }\) is the change of the refraction index. As expressed in Eq. (69), the measured data from the strain sensor are a combination of two factors. The first part is the actual strain of the material including any mechanical strain and strain due to temperature changes. The second part is the wavelength shift due to a change in the glass-refraction index of optical fibre with temperature. According to the FBG sensors manufacturer, 1 °C temperature variation induced strain of optical fibre itself is approximately equivalent to eight micro-strain. Under the 100 W and 440 W, the strain measured at the beginning of the microwave radiation in strain sensors 1 and 3 have similar trends of increasing as predicted when the temperature sensors 1 and 3 measurements have close gradients, having higher temperatures than that measured by sensor 2. A sudden drop in the strain measurements of the middle sensors (strain 2) can be observed in both cases soon after the initial surge, labelled as A-B. It instantaneously alters the strains by nearly identical 1162 and 1008 micro-strains (difference between A and B) under 100 W and 440 W, respectively. Such decline in the strain measurements is attributed to an immediate development of a compressive strain in response to the microwave exposure, as hypothesised in Sect. 2. Note that sensor 2 temperature is the lowest amongst the three sensors, in which the thermally induced strain is negligible. Such phenomenon could not be associated with the temperature rise since the temperature change is approximately 12 °C and 5.7 °C from room temperature 19 °C when the sudden drop occurs at point A, which is remarkably lower than 170 °C when post-curing shrinkage is introduced as indicated by the exothermic peak in the DSC spectra in Fig. 14, and lower than the \({T}_{g}\) to have any detrimental effect. Moreover, it is observed that unloading the specimen from the 440 W exposure results in a residual compressive strain in all sensors’ locations. This occurs after the high non-linear variation of strains in the case of 440 W, unlike the linear strain behaviour under 100 W. This is analogous to mechanical field introduction in which unloading an elastic–plastic specimen beyond its elastic regime under tensile loading may introduce a compressive residual strain distribution depending on the hardening behaviour (i.e. kinematic or isotropic). Further investigation was conducted on the phenomena observed, described as follows:
Different FBG arrays have been adhesively bonded at the same location on the surface of two specimens made of 15 wt.% with identical geometric dimensions and the location of the two specimens are placed at the exact location inside the microwave cavity. Accordingly, the distribution of microwaves in both cases is considered to be identical, also verified using thermal camera. The strain and temperature change measurements of sensor 2 under 100 W and 440 W before and after the ‘sudden drop’ is presented in Fig. 22a–d. It can be observed from Fig. 22a,b that the measured strains demonstrated a steady step-wise increase with the increasing temperature that fluctuated within a constant range of approximately 8 °C. The fluctuations in temperature change exhibit a periodic pattern that is approximately in phase with every step of the increment in strain. Under 440 W as shown in Fig. 22c,d, the increase in the strain and temperature data follow a similar trend as that under 100 W but at a higher rate.
Strain and temperature variations measured by sensor 2 before and after the ‘sudden drop’ at 100 W (a, b) and 440 W (c, d).
In contrast with the middle sensors, the strain and temperature increments from sensor 1 under 100 W and 440 W are predominately synchronized as presented in Fig. 23. It could be observed from Fig. 23a,c that the cycle time for each step is approximate 20 s and each step is approximately 100 micro-strain. A similar trend is also observed in the first 50 s of the microwave exposure under 440 W from Fig. 23b. However, the cycle time for each step shown in Fig. 23d falls sharply to 2 s accompanying a higher increment of 300 micro-strain compared with the 100 W data which are attributed to the increased heating rate at higher microwave power.
Strain and temperature measurements of FBG sensor 1 of (a) and (c) 15 wt.% BaTiO3/Epoxy nanocomposite sample under 100 W for 600 s, (b) and (d) 15 wt.% BaTiO3-Epoxy nanocomposite sample under 440 W for 148 s.
Adhesive FBG data:
Despite the widely known utilisation of FBG strain sensors, there exists a layer of adhesive and protective coating that may affect the data from the nanocomposite102. The FBG sensors are adhesively bonded to the surface of specimens by PERMABOND 920 Cyanoacrylate. The dielectric and thermal properties of the adhesive and neat epoxy are presented in Table 2.
Five FBG sensor arrays, 20 mm apart, were utilised to quantify the adhesive's response distribution. Figure 24 presents the strain and temperature change measured via sensors bonded to a PTFE block with adhesive under 100 W and 440 W. It can be observed from Fig. 24 that temperature increases in the adhesive with microwave exposure time at both power levels as predicted while the temperature rise has a higher rate under 400 W. The maximum temperature changes are around 7 °C and 4.5 °C for 100 W and 440 W, respectively. The insignificant amount of temperature rise is the direct evidence of relative less interaction of adhesive and microwave. The strain values steadily increase with the temperature rise in both cases due to the thermal expansion of PTFE and adhesive. The calculated thermal strain of PTFE based on Fig. 24 and Table 2 under 100 W is approx. 868 micro-strain at 7 °C temperature change. The calculated value is almost consistent with the measured value of strain sensor 1 which is approx. 960 micro-strain at similar temperature variation range. Unlike 100 W, the measured strain of sensor 1 in 440 W shown as the blue line (when microwaves are removed) is approximately 10 micro-strain, which is much lower than 458 microstrain, the calculated thermal strain of PTFE at the same temperature change (3.7 °C).
Strain and Temperature evolution measurements via FBG sensors in adhesive (Permabond 50) bonded on the surface of the PTFE holder under 100 W for 650 s and 440 W for 110 s.
At the microwave exposure, the adhesive solely interacts with the microwave, and is heated up owing to its higher dielectric loss compared with the PTFE. However, the PTFE have a higher CTE than the adhesive. Consequently, the measured strain under 100 W is mainly attributed to the thermal expansion of PTFE from the conduction of heat. The strain sensors under 100 W showed strain increase initiated after 200 s, indicating that a substantial amount of time is required to trigger the heating conduction between the adhesive and PTFE. On the contrary, 440 W has a higher rate of temperature rise within 110 s exposure. Based on the analysis of the calculated and measured strain, the strain under 100 W is mainly attributed to PTFE thermal expansion while the strain under 440 W is dominated by the thermal expansion of adhesive. Under 440 W, a similar trend in temperature rise is noted between sensors 1 and 3, as well as sensor 2 and 4, which is described by the ‘hot spot’ theory due to non-uniform microwave field.
Neat Epoxy FBG data:
Strain and temperature evolution of the neat epoxy with adhesively bonded arrays together under microwave are presented in Fig. 25. The microwave running time has been estimated to maintain the temperature well below the \({{\varvec{T}}}_{{\varvec{g}}}\) of the BaTiO3-epoxy nanocomposite. The temperature increases as a function of the exposure duration (equivalently, microwave energy). Sensor 5 data present a higher rate of temperature variation compared with the other sensors conforming to the ‘hot spot’ theory. The region in which sensor 5 is located within the zone with a higher rate of temperature rise that is denoted as a ‘hot spot’ zone presented in Fig. 26, hence the next hot spot shown in Fig. 26 (red square symbol) is half (60 mm) of the microwave wavelength (120 mm) is located between sensors 3 and 2. As schematically demonstrated, the rest of the FBG sensors are located out of the hot spot region, and therefore they develop similar rates of temperature under microwave.
Strain and temperature evolution of the neat epoxy sample under 100 W and 440 W.
Schematic illustration of the location of FBG sensors on the neat epoxy surface, 20 mm apart, and standing waves formed in a microwave oven showing hot spots (antinodes) and cold spots (nodes).
Strain and temperature response of the neat epoxy with bonded sensor arrays is investigated under microwave (Fig. 25). The temperature increases as a function of microwave exposure time and starts to drop as soon as the microwave stops as predicted. No sudden drop such as that observed in the nanocomposite is observed for the neat epoxy which indicates the phenomenon linked with the embedded BaTiO3. Sensor 5 presents a higher rate of temperature change compared with the other sensors, corresponding to the ‘hot spot’ theory discussed formerly, and illustrated in Fig. 26. As schematically shown in Fig. 26, the other FBG sensors are located out of the hot spot region, and therefore develop similar rates of temperature variation under microwave.
The temperature change in both cases reached the highest value of 30 °C compared with that measured for the adhesive only. The measured strain follows a increasing trend with the temperature change, which is a resultant of the thermal expansion from the adhesive and neat epoxy. Maximum strain and temperature values measured by left-side sensor for adhesive on PTFE (sensor 5), adhesive on epoxy (sensor 5), and adhesive on nanocomposite (sensor 1) are tabulated in Table 3, summarised from the data shown in Figs. 19 and 20, under 100 W and 440 W exposure.
The measured strain of the first two categories (adhesive on PTFE and adhesive on the neat epoxy) are temperature compensated which means the effect of thermal expansion from the optical fibre itself is eliminated. Approximately 8 micro-strain is achieved by a 1 °C change in temperature according to the manufacture. The true strain of the epoxy nanocomposites samples is then lower than the measured strain from sensor 1:
For the case of 100 W exposure, the measured strain of adhesive on PTFE is mainly attributed to the thermal expansion of the PTFE, as formerly discussed. When the FBG arrays are adhesively bonded to a neat epoxy sample, the measured strain drops by approx. 52% compared to that (790 micro-strain) from the sensor adhesively bonded on PTFE at the same temperature variation of 5 °C. It is due to the lower CTEs of epoxy and adhesive compared to that of the PTFE. Furthermore, at this temperature change (5 °C), the measured strain without temperature compensation of epoxy nanocomposites loaded with BaTiO3 drops 35% compared with the neat epoxy. However, as temperature change rises to 30 °C, the measured strain in both cases tends to be similar. Under 440 W, the value of strain is mostly dominated by adhesive as described earlier. When the temperature change firstly reaches 5 °C at the beginning of the microwave exposure, the neat epoxy and nanocomposites have similar strain (320 and 330 micro-strain, respectively).
Raman spectroscopy was utilised to examine any residual/remnant strain induced by the particles to the surrounding epoxy matrix, or any crystal structure transformation of BaTiO3 particles that might be introduced by the microwave exposure. The middle region of the samples where the ‘sudden drop’ in strain occurred was of particular interest, hence it was the region where the laser was focused to obtain the Raman spectra. Another run at microwave power of 1000 W for 50 s was performed for such effect.
Raman characterisations have initially been performed on the neat epoxy and BaTiO3-epoxy nanocomposite samples with 15 wt.% prior to microwave to establish baseline curves for identification of possible change in the position of Raman peaks for the samples post microwave exposure. Raman spectra of the epoxy are shown in Fig. 27a. Broader peaks at 600–800 cm−1 and 800–1000 cm−1 are presented in Fig. 27a for the neat epoxy indicating an amorphous structure. The Raman spectra on three random points within the region of interest of the 15 wt.% Si-BaTiO3 epoxy nanocomposite (Fig. 27b) present a good consistency with 260 cm−1 and 515 cm−1 as characteristic peaks of BaTiO3, and 304 cm−1 indicating the tetragonal phase of BaTiO3 representing the out-of-phase and axial motion of the two oxygen atoms facing oppositely107,108. The stretching mode of Si–O from silane functionalisation on the particle surface is presented as peaks at 641 cm−1 and 826 cm−1109. Raman spectra of the samples before and after microwave exposure at 440 W at room temperature are shown in Fig. 27c. Another run at 1000 W for 50 s was performed with Raman performed at the same location as that at 440 W, presented in Fig. 27d. No conspicuous differences are observed, and it could be noticed that the 304 cm−1 still emerges without recognizable changing in peak height, which implies no changes in the crystal structure of BaTiO3 after the microwave exposure, and no or slight remnant strain field.
Raman spectra of (a) neat epoxy, (b) three random points of 15 wt.% epoxy nanocomposites with Si-BaTiO3 before microwave exposure, (c) 15 wt.% epoxy nanocomposites with Si-BaTiO3 before and after microwave exposure of 440 W for 150 s (d) 15 wt.% epoxy nanocomposites with Si-BaTiO3 before and after microwave exposure of 1000 W for 60 s.
It was observed from the FBG test results that the overall strain measurements of the 15 wt.% BaTiO3-epoxy nanocomposites are relatively smaller compared to those of the neat epoxy under 100 W and 440 W. The strain measurements of the nanocomposites from the beginning of the microwave exposure (ΔT = 5 °C) to a later stage (100 W: ΔT = 30 °C 440 W: ΔT = 21 °C) from sensor 1 data are presented as blue triangle marks in Figs. 28 and 29. The strain measurements of the nanocomposites shown in Figs. 19, 20, and Table 3 have not been corrected to account for the temperature effect of fibre refraction index, while the results presented as blue triangle symbols in Figs. 28 and 29 are corrected values accounting for such effect. Strain measurements of the neat epoxy are also presented as red circle symbols to evaluate the mechanical strain induced by dielectric heating under the exposure.
Evolution of micro-strain with temperature rise—theoretically calculated thermal expansion of adhesive (black), actual strain data from sensor 5 of adhesive bonded onto neat epoxy (red), and actual strain data from sensor 1 of adhesive bonded to 15 wt.% BaTiO3-epoxy nanocomposite (blue) under 100 W at 5 °C, 10 °C, 15 °C, 20 °C, 25 °C, and 30 °C.
Evolution of micro-strain with temperature rise—theoretically calculated thermal expansion of adhesive (black), actual strain data from sensor 5 of adhesive bonded onto neat epoxy (red), and actual strain data from sensor 1 of adhesive bonded to 15 wt.% BaTiO3-epoxy nanocomposite (blue) under 440 W at 5 °C, 10 °C, 15 °C, and 21 °C.
It could be observed from the figures that the measured strain of the nanocomposite (blue triangles) are generally smaller than that of the neat epoxy (red circles). Notably, the difference increases with increasing temperatures under 440 W.
It is well known that the mechanical properties such as elastic modulus, Poisson's ratio, and shear modulus110,108,112 and the CTE113,111,112,116 are strongly dependent upon the microcracks in the matrix. Camahort et al.117 correlated a reduction of the CTEs of thermal cycled composite laminates in the specimens with microcracks identified under the microscope. A theoretical study of the CTEs in cracked laminates demonstrated that CTEs change as a function of the internal stress field115. This discrepancy in CTEs under different internal stress fields is due to the fact that the internal stresses induced by thermal cycling could be either tensile or compressive. When the stress field is tensile, the microcracks further opened up and cause a reduction in the value of CTE. Therefore, this correlation between the microcracks and CTEs might provide an explanation of the reduced strain measurements presented previously. Under microwave, domain wall movements are triggered in the BaTiO3 nanoparticles, hence stress fields around the microcracks might be changed and lead to a different CTE of the nanocomposite as illustrated in Fig. 30.
Schematic of the 15 wt.% BaTiO3-epoxy nanocomposite under exposure at different scales.
It is found by many studies that the CTE of composite material is highly dependent upon its constituents118,119. A decrease in the CTE of the nanocomposite material is observed and is attributed to a relative lower CTE of the fillers compared with that of the epoxy matrix [Dittanet, P., The use of nanosilica in epoxy resins, in Polymer Science and Engineering. 2008, Lehigh University]. The CTE of BaTiO3 and Epoxy is 1 microstrain/°C and 75 microstrain/°C [Khaleque, T., et al., Tailoring of Thermo-Mechanical Properties of Hybrid Composite-Metal Bonded Joints. Polymers, 2021. 13(2)]. The curing of BTO/Epoxy samples starts simultaneously with the temperature rising due to the microwave heating effect. However, under relatively lower temperatures, the curing effect is neglectable (exothermic peak can be seen from the DSC graph as curing is an exothermic reaction). The temperature of microwave heating is controlled below 50 °C which is below the exothermic peak around 170 °C. Therefore, the curing shrinkage effect is not significant during microwave radiation.
The average crystallite size of the purchased BaTiO3 nanoparticles are determined by XRD results using Scherrer's equation120:
where \(k\) is the dimensionless shape factor of the crystallite, \(\lambda\) is the X-ray wavelength, \(2\theta\) is the peak position, \(B\left(2\theta \right)\) is the half-width of the maximum intensity of the peak and \(\theta\) is the Bragg diffraction angle. A round-up value of 1.0 is selected in this study. The mean crystallite size is 35.9 nm, and it indicates that the corresponding grain size is 35.9 nm in the 200 nm BaTiO3 nanoparticles as shown in Fig. 31. Note that the strain measured by the sensors is averaged over a 5 mm × 0.5 mm region (i.e. sensor size). Such sensing area covers approximately 890,000 200 nm-particles, or alternatively 70 particles over a 20 × 20 µm2 area.
Nanocrystalline structure of BaTiO3 nanoparticles well-dispersed within the area over which the extrinsic strains are measured by the FBG sensors.
The black square marks in Figs. 28 and 29 represent the theoretically calculated values of linear thermal expansion of the adhesive used for bonding the FBG arrays. It can be observed that the strains in the neat epoxy are slightly lower than those measured by the thermal expansion of the adhesive at an identical temperature. A schematic diagram of the cross-section of an FBG array bonded to the sample is presented in Fig. 32. As discussed for Figs. 24 and 25, the adhesive exhibits lower interaction with microwave, hence a poorer dielectric heating effect. Thus, when the exposure initiated, the neat epoxy is firstly heated up due to the microwave selective heating based upon its different dielectric loss. The energy is then transferred to the adhesive via heating conduction from the epoxy, which initiates a thermal expansion in the adhesive. However, the epoxy possesses a relatively lower CTE in comparison with that of the adhesive. Consequently, the thermal expanding rates are different due to the mismatch in CTEs. As such, the measured strain in the FBGs is a result of thermal expansion of the adhesive constrained (via bonding) by the epoxy, causing the FBG arrays to bend with increasing temperature and bend back when the temperature drops. This behaviour might also be an explanation of the ‘zig-zag’ step-wise increment observed in Fig. 23. When the temperature ramping rate is slower under 100 W, the heat transfer between the epoxy and the adhesive is steadier compared with that under 440 W. Subsequently, the strain measurements exhibit a clearer step-wise increment under 100 W.
Schematic diagram of adhesively bonded FBG arrays to the sample's surface and non-uniform thermal expansion due to mismatch in CTEs.
It is also noteworthy that the unanticipated finding of a ‘sudden drop’ during real-time strain measurement of the middle FBG sensor (presented in Figs. 19 and 20) occurs at the beginning of the microwave exposure at 1045 micro-strain under 100 W and 1261 micro-strain under 440 W, which is a clear implication of a phenomenologically induced compressive strain in the multi-material system around the middle FBG sensor. The true reason for the occurrence of this phenomenon remains unclear, however since the temperature effects are excluded and the phenomenon is only seen in the nanocomposite (and not in the neat epoxy), such high extrinsic strain variation is strongly attributed to the collective domain wall movements due to the reorientation of dipoles at high frequency in each domain.
As the microwave travels through the material, the microwave power decays due to the absorption by the material as it penetrates. As a result, the distribution of the microwave field within the material is non-uniform. For the 15 wt.% BaTiO3-epoxy nanocomposites, the penetration depth calculated by Eq. (61) is approximately 0.86 m, based on the measured dielectric properties at 2.5 GHz. This value indicates that approximately 63% of the energy from the incident microwave is dissipated at this distance under the sample surface. Therefore, for a nanocomposite with 3-mm thickness, it would be a reasonable assumption to make that the microwave fully penetrates the sample. Apart from the non-uniformity caused by the penetration depth of the microwave, there is also another factor that affects the non-uniform electric field distribution in the material, which is the standing waves formed in the microwave oven, extensively studied121,119,123. When the microwave field transmits and reflects within the cavity of the microwave oven, the standing waves form, and the ‘hot spot’ phenomenon manifests. The distance between two ‘hot spots’ is half of the wavelength of the incident microwave, which is approximately 60 mm. Therefore, the temperature change measured by FBG sensors exhibit different heating rates along with the 130 mm sample.
The power absorbed by the material is evaluated by the method of the energy balance of the microwave heating effect. At power 100 W, the average power per unit area in the 354 × 338 mm2 microwave oven is calculated as follows:
From Eqs. (62) and (63), the peak electric field strength \(E\) m and root-mean-square \({E}_{rms}\) of the incident microwave field is:
Similarly, for the 440 W microwave power level, the peak electric field strength \({E}_{m}\) is 1.67 × 103 V/m, and the \({E}_{rms}\) is 1.18 × 103 V/m. The estimated electric field is the power absorbed by the air. However, it is assumed that when the microwave field generation is initiated by the magnetron, the electric field strength within the microwave oven is assumed to be equivalent to the value of the \({E}_{rms}\) as the dimension of the sample (4 cm3) is relatively smaller than the cavity size (27,520 cm3). The energy absorbed as a function of time calculated based on the \({E}_{rms}\) calculated above is estimated as follows:
The strain and temperature measurements as a function of energy absorbed in Joules are presented below, under 100 W and 440 W.
It could be observed from Figs. 33 and 34 that, the energy absorption rate is close to the rate of temperature rise in the FBG sensors. At the beginning of the microwave exposure, the temperature rise exhibits a similar rate compared with the energy absorption rate. As the exposure time increases, the temperature rise becomes significantly slower. The ‘hot spot’ theory due to the non-uniformity of microwave fields is proposed to be the possible explanation of this phenomenon as described formerly.
Temperature change measurements (micro-strain) by FBG sensors (left), and energy absorbed (right) versus time (s) under 100 W.
Temperature change measurements (micro-strain) by FBG sensors (left), and energy absorbed (right) versus time (s) under 440 W.
The internal electric field inside the sample could only be estimated based on the assumption that 100% energy transfers into heat. Therefore, the external electric field of the incident microwave at the surface of the BaTiO3-Epoxy sample, \({E}_{rms, external}\) is obtained from Eq. (66), and employed to be the \({E}_{rms}\) to solving the Eq. (22) to estimate the eigenstrain of the BaTiO3.
where calculated \(\rho\) by given weight and volume is 1.3 g/cm3, \(C\) calculated from the DSC spectra is 1.238 J.g-1.°C−1, \(a\) is sample thickness 3 mm, \(c\) is the speed of microwave (3 × 1010 cm/s), \({\varepsilon }_{0}\) is the permittivity of the free space (8.85 × 10−14 F/cm), and \(\xi\) and \(\Gamma\) is calculated by Eq. (67), Eq. (68), as follows:
where \({d}_{p}\) is calculated to be 850 mm, \({n}_{1}\) is 1 for air and \({n}_{2}=\sqrt{{\varepsilon }^{^{\prime}}}=\sqrt{4.42}\).
At the beginning of the exposure when the microwave incident the sample at \(t=10s\) under 100 W, the rate of temperature rise \(\frac{\Delta T}{\Delta t}\) is obtained using the linear fit of the temperature change measurements from FBG sensor 1, which is 0.05.
The eigenstrain of BaTiO3 nanoparticle movements based on the simplified model of Eqs. (21) and (22) at 100 W, \({\varepsilon }_{BaTiO_{3}}\) is:
where \({P}_{0}\) is 0.26 C/m2, \(Y\) is the young's modulus of BaTiO3, which is assumed 13.6 × 108 N/cm252.
The domain width \(d\) is highly dependent on the grain/crystallite size, therefore, it is estimated to be 4 × 10−5 cm with the crystallite size assumed to be equal to the nanoparticle size 200 nm based on the measurements in previous studies124, and the strain \({\varepsilon }_{440}\) at \(t=7s\) under 440 W with the rate of temperature rise of 0.3, is \(144\times {10}^{-6}\). This value could only represent the approximate amplitude of the induced DW displacement under such electric field that impinges the sample surface.
As discussed in Sect. 3, the electric field-induced strain is predominately attributed to the irreversible domain wall movement in multi-domain ferroelectric crystals. Therefore, when the microwave field is removed, a residual stress field is hypothesised, and Raman spectroscopy was employed in this study to probe any possible residual strain effects that originate from microwave field activated BaTiO3 nanoparticles. The Raman peaks shift indicated the changes in the atomic spacing of the material, namely the strain information125. In the meantime, it was also discovered that the altered stress state surrounding the BaTiO3 could introduce a crystal structure change due to the piezoelectricity effect exhibit in ferroelectric materials. Raman data did not indicate a significant difference between the Raman spectra of 15 wt.% nanocomposite samples with and without microwave treatment.
The quantitative research on microwave field-nanocomposite interaction was conducted to study the ferroelectric materials’ response in high-performance (rigid) epoxy composite that offers reversible microwave activated electro-strains introduced by a second dielectric phase (BaTiO3). The data presented a pioneering investigation as no investigations have been reported, thus far, on the micromechanical (extrinsic) strain response of rigidly constrained ferroelectric materials in polymer under external electromagnetic fields. The research has characterised the thermal and dielectric properties of ferroelectric nanoparticles (BaTiO3) modified polymer (epoxy) at weight loading up to 15 wt.%, and subsequently investigated the extrinsic strain state induced by the BaTiO3 nanoparticles’ dipole displacements onto their surrounding epoxy, however observed at the phenomenological level in the multi-material system. Silane surface functionalisation of the nanoparticles was utilised to uniformly disperse and improve interfacial particle–matrix bonding quality. FBG sensors-based technique was employed, in-situ with the microwave exposure, for real-time monitoring of the strain and temperature response of the nanocomposite subjected to a 2.45 GHz microwave field at controlled exposure power and energy, followed by theoretical constitutive equations underpinning field-material interactions, and the remnant extrinsic strain investigations using Raman spectroscopy. The key remarks on the investigations conducted in this article are as follows:
A time-dependent strain field is introduced, proportional to the exposure time/energy, in the multi-domain BaTiO3 nanoparticles under the stimulation of a microwave field, linearly under 100 W and non-linearly under 440 W. The strain is theoretically described via development of multi-physics constitutive expressions for the nanoparticle possessing a multi-domain crystallite based on an estimated electric field strength exhibiting at the geometric boundary of the particle.
The principle of virtual work was utilised, phenomenologically for the theoretical development, to estimate the strain within the epoxy matrix embedded with BaTiO3 subjected to the microwave exposure, able to underpin the in-situ induced micro-straining performance of the BaTiO3-epoxy nanocomposite.
A sudden drop in micro-strain data by the value of approx. 1000 compressive micro-strains was observed in the BaTiO3-epoxy composites at the beginning phase of the exposure under the different exposure powers examined. Such phenomenon has not been reported thus far in the existing literature, however investigated herein using different characterisation and theoretical development at micromechanical level. The drop indicated an instantaneously induced compressive strain achieved within a small fraction of a second, which is recovered afterwards with the increasing exposure energy, followed by a gradual increase during the exposure. No arcing in the microwave was observed, and no damage in any part of the FBG, adhesive, composite and PTFE; The temperature variation due to the exposure was kept well below the \({T}_{g}\), and the DSC investigations presented a fully cured nanocomposite. The theoretical–experimental study of the response led to the fact that such effect is caused by the DW movement response of the BaTiO3-epoxy composite under microwave exposure, which is attributed to a mechanical compressive field to its surrounding polymer, with its effect phenomenologically observed by the in-situ FBG technique.
The nanocomposite exhibited linear and highly non-linear strain variations under the 100 W and 440 W exposure, respectively. Residual compressive strains were developed post 440 W exposure, offering an analogous response to the mechanical field pre-straining which takes the strain hardening materials (e.g. polycrystalline) beyond its elastic regime. Such strain hardening response in the case of 440 W is attributed to the semi-crystalline phase that BaTiO3 had introduced to the nanocomposite.
To achieve the full benefit from the electro-strain behaviour of the BaTiO3 fillers, uniform dispersion of the nanoparticles in the epoxy matrix was considered to be the primary determinant factor. Large agglomerates were observed in non-functionalised BaTiO3-epoxy nanocomposites due to the attraction between the nano-scale particles, and their intrinsic incompatibility with hydro-carbon epoxy matrix. Uniform dispersion of the surface functionalised BaTiO3 nanoparticles ensures a uniform application of the domain wall movements triggered stress field to their surrounding epoxy matrix. Furthermore, it also avoids the possible negative attributes from large agglomerations to the mechanical performances, as the aggregation of nanoparticles might act as a weak spot compared with the uniform dispersed nanoparticles. The efficiency of silane functionalisation on the uniform dispersion of BaTiO3 nanoparticles was demonstrated.
Ozdemir, N. G. et al. Toughening of carbon fibre reinforced polymer composites with rubber nanoparticles for advanced industrial applications. Express Polym. Lett. 10(5), 394–407 (2016).
Article CAS Google Scholar
Yazdani Nezhad, H., Stratakis, D., Ayre, D., Addepalli, S. & Zhao, Y. Mechanical performance of composite bonded joints in presence of localised process-induced zero-thickness defects. Procedia Manuf. 16, 91–98 (2018).
Yazdani Nezhad, H., Merwick, F., Frizzell, R. M. & McCarthy, C. T. Numerical analysis of low-velocity rigid-body impact response of composite panels. Crashworthiness 20(1), 27–43 (2015).
Hernandez, T. P. A., Mills, A. R. & Yazdani Nezhad, H. Shear driven deformation and damage mechanisms in High-performance carbon Fibre-reinforced thermoplastic and toughened thermoset composites subjected to high strain loading. Compos. Struct. 261, 113289 (2021).
Ratna, D. & Banthia, A. K. Rubber toughened epoxy. Macromol. Res. 12(1), 11–21 (2004).
Article CAS Google Scholar
Ma, J. et al. Effect of inorganic nanoparticles on mechanical property, fracture toughness and toughening mechanism of two epoxy systems. Polymer 49(16), 3510–3523 (2008).
Article CAS Google Scholar
Thostenson, E. T. & Chou, T.-W. Processing-structure-multi-functional property relationship in carbon nanotube/epoxy composites. Carbon 44(14), 3022–3029 (2006).
Article CAS Google Scholar
Eqra, R., Janghorban, K. & Daneshmanesh, H. Mechanical properties and toughening mechanisms of epoxy/graphene nanocomposites. J. Polym. Eng. 35(3), 257–266 (2015).
Article CAS Google Scholar
Liu, T. et al. Morphology and fracture behavior of intercalated epoxy/clay nanocomposites. J. Appl. Polym. Sci. 94(3), 1236–1244 (2004).
Article CAS Google Scholar
An, Q., Rider, A. N. & Thostenson, E. T. Hierarchical composite structures prepared by electrophoretic deposition of carbon nanotubes onto glass fibers. ACS Appl. Mater. Interfaces 5(6), 2022–2032 (2013).
Article CAS PubMed Google Scholar
Lin, M.-S., Liu, C.-C. & Lee, C.-T. Toughened interpenetrating polymer network materials based on unsaturated polyester and epoxy. J. Appl. Polym. Sci. 72(4), 585–592 (1999).
3.0.CO;2-M" data-track-action="article reference" href="https://doi.org/10.1002%2F%28SICI%291097-4628%2819990425%2972%3A4%3C585%3A%3AAID-APP15%3E3.0.CO%3B2-M" aria-label="Article reference 11" data-doi="10.1002/(SICI)1097-4628(19990425)72:43.0.CO;2-M">Article CAS Google Scholar
Kinloch, A. and Young R. J. Fracture behaviour of polymer. Applied Science Publishers, London and New York (1983).
Kinloch, A. J. et al. Deformation and fracture behaviour of a rubber-toughened epoxy: 1. Microstructure and fracture studies. Polymer 24(10), 1341–1354 (1983).
Article CAS Google Scholar
Park, S.-J., Jin, F.-L. & Lee, C. Preparation and physical properties of hollow glass microspheres-reinforced epoxy matrix resins. Mater. Sci. Eng. A 402(1), 335–340 (2005).
Article CAS Google Scholar
Wu, D. Y., Meure, S. & Solomon, D. Self-healing polymeric materials: A review of recent developments. Prog. Polym. Sci. 33(5), 479–522 (2008).
Article CAS Google Scholar
Low, I. M. Effects of residual stresses on the failure micromechanisms in toughened epoxy systems. J. Mater. Sci. 25(4), 2144 (1990).
Article ADS CAS Google Scholar
Karger-Kocsis, J. et al. Interphase Engineering with Nanofillers in Fiber-Reinforced Polymer Composites 71–101 (John Wiley & Sons, Inc., Hoboken, 2016).
Google Scholar
Garg, A. C. & Mai, Y. W. failure mechanisms in toughened epoxy-resins - a review. Compos. Sci. Technol. 31(3), 179–223 (1988).
Article CAS Google Scholar
Tsai, J.-L., Huang, B.-H. & Cheng, Y.-L. Enhancing fracture toughness of glass/epoxy composites by using rubber particles together with silica nanoparticles. J. Compos. Mater. 43(25), 3107–3123 (2009).
Article ADS CAS Google Scholar
Singh, R. P., Zhang, M. & Chan, D. Toughening of a brittle thermosetting polymer: Effects of reinforcement particle size and volume fraction. J. Mater. Sci. 37(4), 781–788 (2002).
Article ADS CAS Google Scholar
Liu, H. & Brinson, L. C. Reinforcing efficiency of nanoparticles: A simple comparison for polymer nanocomposites. Compos. Sci. Technol. 68(6), 1502–1512 (2008).
Article CAS Google Scholar
Nezhad, H. Y. & Thakur, V. K. Effect of morphological changes due to increasing carbon nanoparticles content on the quasi-static mechanical response of epoxy resin. Polymers 10(10), 1106 (2018).
Article PubMed Central CAS Google Scholar
Bregar, T. et al. Carbon nanotube embedded adhesives for real-time monitoring of adhesion failure in high performance adhesively bonded joints. Sci. Rep. 10(1), 16833 (2020).
Article ADS CAS PubMed PubMed Central Google Scholar
Sprenger, S. Epoxy resin composites with surface-modified silicon dioxide nanoparticles: A review. J. Appl. Polym. Sci. 130(3), 1421–1428 (2013).
Article CAS Google Scholar
Liu, K. W. & Macosko, C. W. Can nanoparticle toughen fiber-reinforced thermosetting polymers?. J. Mater. Sci. 54(6), 4471–4483 (2019).
Article ADS CAS Google Scholar
Domun, N. et al. Improving the fracture toughness and the strength of epoxy using nanomaterials - a review of the current status. Nanoscale 7(23), 10294–10329 (2015).
Article ADS CAS PubMed Google Scholar
Vahedi, V., Pasbakhsh, P. & Chai, S.-P. Toward high performance epoxy/halloysite nanocomposites: New insights based on rheological, curing, and impact properties. Mater. Des. 68, 42–53 (2015).
Article CAS Google Scholar
Awaja, F. et al. Cracks, microcracks and fracture in polymer structures: Formation, detection, autonomic repair. Prog. Mater Sci. 83, 536–573 (2016).
Article CAS Google Scholar
Low, I. M. Toughening of epoxies by thermal expansion mismatch. J. Appl. Polym. Sci. 39(3), 759–762 (1990).
Article CAS Google Scholar
Kim, N. H. & Kim, H. S. Toughening method and mechanisms for thermosets. J. Appl. Polym. Sci. 98(4), 1663–1667 (2005).
Article CAS Google Scholar
Damjanovic, D. Contributions to the piezoelectric effect in ferroelectric single crystals and ceramics. J. Am. Ceram. Soc. 88(10), 2663–2676 (2005).
Article CAS Google Scholar
Gerber, P. et al. Effects of reversible and irreversible ferroelectric switchings on the piezoelectric large-signal response of lead zirconate titanate thin films. J. Appl. Phys. 98, 124101–124101 (2005).
Article ADS CAS Google Scholar
Kingon, A. I. & Srinivasan, S. Lead zirconate titanate thin films directly on copper electrodes for ferroelectric, dielectric and piezoelectric applications. Nat. Mater. 4(3), 233–237 (2005).
Article ADS CAS Google Scholar
Manbachi, A. & Cobbold, R. S. C. Development and application of piezoelectric materials for ultrasound generation and detection. Ultrasound 19(4), 187–196 (2011).
Article Google Scholar
Forrester, W. F. & Hinde, R. M. Crystal structure of barium titanate. Nature 156(3954), 177–177 (1945).
Article ADS MathSciNet CAS Google Scholar
Xu, Y. Ferroelectric Materials and Their Applications (Sole Distributors for the USA and Canada, Elsevier Science Pub. Co, Amsterdam, New York, New York, NY, USA, North-Holland, 1991).
Google Scholar
Pramanick, A. et al. Domains, domain walls and defects in perovskite ferroelectric oxides: A review of present understanding and recent contributions. Crit. Rev. Solid State Mater. Sci. 37(4), 243–275 (2012).
Article ADS CAS Google Scholar
Dudhe, C. M. et al. Study of 90 degrees and 180 degrees Nanodomains in BaTiO3 Nanoparticles Using Transmission Electron Microscopy. Ferroelectrics 471(1), 148–155 (2014).
Article CAS Google Scholar
Abel, S. et al. Large Pockels effect in micro- and nanostructured barium titanate integrated on silicon. Nat. Mater. 18(1), 42–47 (2019).
Article ADS CAS PubMed Google Scholar
Jo, W. et al. Giant electric-field-induced strains in lead-free ceramics for actuator applications - status and perspective. J. Electroceram. 29(1), 71–93 (2012).
Article CAS Google Scholar
Gao, J. H. et al. Recent progress on BaTiO3-based piezoelectric ceramics for actuator applications. Actuators 6(3), 20 (2017).
Article Google Scholar
Ren, X. B. Large electric-field-induced strain in ferroelectric crystals by point-defect-mediated reversible domain switching. Nat. Mater. 3(2), 91–94 (2004).
Article ADS CAS PubMed Google Scholar
Jacob, J., Chia, L. H. L. & Boey, F. Y. C. Thermal and non-thermal interaction of microwave radiation with materials. J. Mater. Sci. 30(21), 5321–5327 (1995).
Article ADS CAS Google Scholar
Gupta, M. & Eugene, W. W. L. Introduction to Microwaves. In Microwaves and Metals. p. 1–23, Wiley (2007)
Green, M. & Chen, X. Recent progress of nanomaterials for microwave absorption. J. Materiomics 5(4), 503–541 (2019).
Article Google Scholar
Pertsev, N. A. & Arlt, G. Forced translational vibrations of 90-degrees domain-walls and the dielectric-dispersion in ferroelectric ceramics. J. Appl. Phys. 74(6), 4105–4112 (1993).
Article ADS CAS Google Scholar
Ma, L. & Korsunsky, A. M. The principle of equivalent eigenstrain for inhomogeneous inclusion problems. Int. J. Solids Struct. 51(25), 4477–4484 (2014).
Article Google Scholar
Arlt, G. Twinning in ferroelectric and ferroelastic ceramics - stress relief. J. Mater. Sci. 25(6), 2655–2666 (1990).
Article ADS CAS Google Scholar
Nechaev, V. N. & Roschupkin, A. M. On the generalized expression of the configuration force acting on the interfaces and domain boundaries in ferroelectric polycrystals. Ferroelectrics 90(1), 29–34 (1989).
Article Google Scholar
Pertsev, N. A. & Arlt, G. Internal-stresses and elastic energy in ferroelectric and Ferroelastic ceramics - calculations by the dislocation method. Ferroelectrics 123(1–2), 27–44 (1991).
Article CAS Google Scholar
Arlt, G. & Pertsev, N. A. Force-constant and effective mass of 90-degrees domain-walls in ferroelectric ceramics. J. Appl. Phys. 70(4), 2283–2289 (1991).
Article ADS Google Scholar
Arlt, G., Bottger, U. & Witte, S. Emission of GHZ shear-waves by ferroelastic domain-walls in ferroelectrics. Appl. Phys. Lett. 63(5), 602–604 (1993).
Article ADS CAS Google Scholar
DeWit, R. Theory of disclinations: II. Continuous and discrete disclinations in anisotropic elasticity. J. Res. Natl. Bur. Stand. A Phys. Chem. 77(1), 49–100 (1973).
Article Google Scholar
Eshelby, J. D. The determination of the elastic field of an ellipsoidal inclusion, and related problems. Proc. R. Soc. Lond. Ser. A 241, 376 (1957).
Article ADS MathSciNet MATH Google Scholar
Eshelby, J. D. & Peierls R.E. The elastic field outside an ellipsoidal inclusion. In Proceedings of the Royal Society of London. Series A. vol. 252, 561–569 (Mathematical and Physical Sciences, 1959)
Mason, W. P. Micromechanics of defects in solids, by Toshio Mura. J. Acoust. Soc. Am. 73(6), 2237–2237 (1983).
Article ADS Google Scholar
Module 3 Constitutive Equations, Structural Mechanics, MIT. http://web.mit.edu/16.20/homepage/3_Constitutive/Constitutive_files/module_3_with_solutions.pdf.
Arlt, G., Bottger, U. & Witte, S. Dielectric dispersion of ferroelectric ceramics and single-crystals at microwave-frequencies. Ann. Phys. 3(7–8), 578–588 (1994).
Article Google Scholar
Chen, X. et al. Electromagnetic characteristics of barium titanate/epoxide resin composites in X and Ku bands. J. Alloys Compd. 453(1), 433–436 (2008).
Article CAS Google Scholar
Bur, A. J. Dielectric properties of polymers at microwave frequencies: A review. Polymer 26(7), 963–977 (1985).
Article CAS Google Scholar
Vadivambal, R. & Jayas, D. S. Non-uniform temperature distribution during microwave heating of food materials—a review. Food Bioprocess Technol. 3(2), 161–171 (2010).
Article Google Scholar
Dibben, D. Electromagnetics: fundamental aspects and numerical modeling. In Handbook of Microwave Technology for Food Applications. p.1–28, CRC Press (2001).
Saltiel, C. & Datta, A. K. Heat and mass transfer in microwave processing. In Advances in Heat Transfer (eds Hartnett, J. P. et al.) 1–94 (Elsevier, Amsterdam, 1999).
Google Scholar
Ayappa, K. G. et al. Analysis of microwave heating of materials with temperature-dependent properties. AIChE J. 37(3), 313–322 (1991).
Article CAS Google Scholar
Mishra, R. R. & Sharma, A. K. Microwave-material interaction phenomena: Heating mechanisms, challenges and opportunities in material processing. Compos. Part A Appl. Sci. Manuf. 81, 78–97 (2016).
Article CAS Google Scholar
Mgbemena, C. O. et al. Accelerated microwave curing of fibre-reinforced thermoset polymer composites for structural applications: A review of scientific challenges. Compos. A Appl. Sci. Manuf. 115, 88–103 (2018).
Article CAS Google Scholar
Sharma, B. et al. Microwave-assisted rapid synthesis of reduced graphene oxide-based gum tragacanth hydrogel nanocomposite for heavy metal ions adsorption. Nanomaterials 10(8), 1616 (2020).
Article CAS PubMed Central Google Scholar
Sanny, S. J. L. W. M. J. OpenStax University Physics, University Physics Volume 2 Vol. 2. (2019) OpenStax CNX http://cnx.org/contents/[email protected].
Luo, J. Analyses of multimode forming process in a microwave-heating cavity. Piers Online 3, 801–807 (2007).
Article Google Scholar
Fu, Y.-C. et al. An apparatus for on-line measuring electric field intensity during microwave heating: a theoretical consideration. Int. J. Food Sci. Technol. 40(7), 743–757 (2005).
Article CAS Google Scholar
Lorrain, P. C. D. R. Electromagnetic Fields and Waves (W.H. Freeman, San Francisco, 1970).
Google Scholar
Cheng, D. K. Field and Wave Electromagnetics (Addison Wesley, Reading, Mass, 1983).
Google Scholar
US Research Nanomaterials, I. https://www.us-nano.com/inc/sdetail/403. (2020).
Patsidis, A. C. & Psarras, G. C. Structural transition, dielectric properties and functionality in epoxy resin—barium titanate nanocomposites. Smart Mater. Struct. 22(11), 115006 (2013).
Article ADS CAS Google Scholar
Zhou, T. et al. Improving dielectric properties of BaTiO3/ferroelectric polymer composites by employing surface hydroxylated BaTiO3 nanoparticles. ACS Appl. Mater. Interfaces 3(7), 2184–2188 (2011).
Article CAS PubMed Google Scholar
UK, F.S. https://www.fishersci.co.uk/shop/products/hydrogen-peroxide-30-water-fisher-bioreagents/10386643#?keyword=hydrogen+peroxide. (2021).
Ambrożewicz, D. et al. Fluoroalkylsilane versus alkylsilane as hydrophobic agents for silica and silicates. J. Nanomater. 2013, 631938 (2013).
Article CAS Google Scholar
UK, F.S. https://www.fishersci.co.uk/shop/products/ethanol-absolute-200-proof-molecular-biology-grade-fisher-bioreagents-5/16606002. (2021).
Phan, T. T. M. et al. Enhancement of polarization property of silane-modified BaTiO3 nanoparticles and its effect in increasing dielectric property of epoxy/BaTiO3 nanocomposites. J. Sci. Adv. Mater. Devices 1(1), 90–97 (2016).
Article Google Scholar
Sundar, U., Lao, Z. C. & Cook-Chennault, K. Enhanced dielectric permittivity of optimized surface modified of barium titanate nanocomposites. Polymers 12(4), 26 (2020).
Article CAS Google Scholar
Sideridou, I. D. & Karabela, M. M. Effect of the amount of 3-methacyloxypropyltrimethoxysilane coupling agent on physical properties of dental resin nanocomposites. Dent. Mater. 25(11), 1315–1324 (2009).
Article CAS PubMed Google Scholar
Saeed, K., Shafique, M. F., Byrne, M. B. & Hunter, I. C., Planar microwave sensors for complex permittivity characterization of materials and their applications. In Applied Measurement Systems. IntechOpen (2012).
Rovensky, T. et al. Microstrip methods for measurement of dielectric properties in High Frequency area. In 2015 38th International Spring Seminar on Electronics Technology (ISSE). (2015).
Bansal, P., Vineyard, E. & Abdelaziz, O. Advances in household appliances- A review. Appl. Therm. Eng. 31(17), 3748–3760 (2011).
Article Google Scholar
Lijima, M. et al. Surface modification of BaTiO3 particles by silane coupling agents in different solvents and their effect on dielectric properties of BaTiO3/epoxy composites. Colloids Surf. Physicochem. Eng. Asp 352(1–3), 88–93 (2009).
Google Scholar
Lin, C.-Y. et al. Preparation and characterization of organosoluble polyimide/BaTiO3 composite films with mechanical- and chemical-treated ceramic fillers. Polym. J. 44(11), 1131–1137 (2012).
Article CAS Google Scholar
Tomer, V. et al. Epoxy-based nanocomposites for electrical energy storage. I: effects of montmorillonite and barium titanate nanofillers. J. Appl. Phys. 108, 074116 (2010).
Article ADS CAS Google Scholar
Dusek, K. Epoxy resins and composites III. In Advances in Polymer Science 166 (Springer-Verlag, Berlin Heidelberg, Berlin, 1986).
Google Scholar
Zhang, X. et al. Polyaniline stabilized barium titanate nanoparticles reinforced epoxy nanocomposites with high dielectric permittivity and reduced flammability. J. Mater. Chem. C 1(16), 2886–2899 (2013).
Article ADS CAS Google Scholar
Tian, L. H. et al. Effect of hydrogenation on the microwave absorption properties of BaTiO3 nanoparticles. J. Mater. Chem. A 3(23), 12550–12556 (2015).
Article CAS Google Scholar
Cheng, K. C. et al. Dielectric properties of epoxy resin-barium titanate composites at high frequency. Mater. Lett. 61(3), 757–760 (2007).
Article CAS Google Scholar
Ramajo, L., Castro, M. S. & Reboredo, M. M. Effect of silane as coupling agent on the dielectric properties of BaTiO3-epoxy composites. Compos. Part A Appl. Sci. Manuf. 38(8), 1852–1859 (2007).
Article CAS Google Scholar
Popielarz, R. et al. Dielectric properties of polymer/ferroelectric ceramic composites from 100 Hz to 10 GHz. Macromolecules 34(17), 5910–5915 (2001).
Article ADS CAS Google Scholar
Schulze, G. J. Ferroelectric crystals. ZAMM J. Appl. Math. Mech. Z. Angew. Math. Mech. 43(10–11), 512–512 (1963).
Article Google Scholar
Yang, W. H. et al. A systematic study on electrical properties of the BaTiO3-epoxy composite with different sized BaTiO3 as fillers. J. Alloys Compd. 620, 315–323 (2015).
Article CAS Google Scholar
Chen, R.-C. et al. Chemically bonding BaTiO3 nanoparticles in highly filled polymer nanocomposites for greatly enhanced dielectric properties. J. Mater. Chem. C 8(26), 8786–8795 (2020).
Article ADS CAS Google Scholar
Wendel, L. Dielectric Measurements at GHz Frequencies (Universitätsbibliothek der Universität Stuttgart, Stuttgart, 2019).
Google Scholar
Huang, X. et al. Polyethylene/aluminum nanocomposites: Improvement of dielectric strength by nanoparticle surface modification. J. Appl. Polym. Sci. 113(6), 3577–3584 (2009).
Article CAS Google Scholar
Kok, L. P., Boon, M. E. & Smid, H. M. The problem of hot spots in microwave equipment used for preparatory techniques—Theory and practice. Scanning 15(2), 100–109 (1993).
Article Google Scholar
Sun, J., Wang, W. L. & Yue, Q. Y. Review on microwave-matter interaction fundamentals and efficient microwave-associated heating strategies. Materials 9(4), 231 (2016).
Article ADS PubMed Central CAS Google Scholar
Kreuzer, M. Strain Measurement with fiber bragg grating sensors. HBM, Darmsdtadt, Germany (2006).
Her, S.-C. & Huang, C.-Y. Thermal strain analysis of optic fiber sensors. Sensors 13(2), 1846–1855 (2013).
Article ADS PubMed PubMed Central Google Scholar
Rajesh, S. et al. Microwave dielectric properties of PTFE/rutile nanocomposites. J. Alloys Compd. 477(1), 677–682 (2009).
Article CAS Google Scholar
Kirby, R. K. Thermal expansion of polytetrafluoroethylene (Teflon) From - 1900 to +3000 C. J. Res. Natl. Bureau Stand. 57(2), 91 (1956).
Article CAS Google Scholar
PERMABOND® 920 Cyanoacrylate Technical Datasheet, PQCY00035-tds, P.E. Adhesives (2016). https://www.glueonline.co.uk/pdf/TDS/PQCY00035-tds.pdf.
Khaleque, T. et al. Tailoring of thermo-mechanical properties of hybrid composite-metal bonded joints. Polymers 13(2), 170 (2021).
Article CAS PubMed Central Google Scholar
Chen, X. D. et al. Microwave absorption properties of barium titanate/epoxide resin composites. J. Phys. D-Appl. Phys. 40(6), 1827–1830 (2007).
Article ADS CAS Google Scholar
Baek, K. et al. Axial oxygen vacancy-regulated microwave absorption in micron-sized tetragonal BaTiO3 particles. J. Mater. Chem. C 6(36), 9749–9755 (2018).
Article CAS Google Scholar
Siniscalco, D. et al. Functionalization of hydroxyapatite ceramics: raman mapping investigation of silanization. Ceramics 2(2), 372–384 (2019).
Article CAS Google Scholar
Dvorak, G. J., Laws, N. & Hejazi, M. Analysis of progressive matrix cracking in composite laminates I. Thermoelastic properties of a ply with cracks. J. Compos. Mater. 19(3), 216–234 (1985).
Article ADS Google Scholar
Talreja, R. Transverse cracking and stiffness reduction in composite laminates. J. Compos. Mater. 19(4), 355–375 (1985).
Article ADS CAS Google Scholar
Smith, P. A. & Wood, J. Poisson's ratio as a damage parameter in the static tensile loading of simple Crossplv laminates. Compos. Sci. Technol. Compos. Sci. Technol 38, 85–93 (1990).
Article Google Scholar
Bowles, D. E. Effect of microcracks on the thermal expansion of composite laminates. J. Compos. Mater. 18(2), 173–187 (1984).
Article ADS CAS Google Scholar
Lim, S. G. & Hong, C. S. Effect of transverse cracks on the thermomechanical properties of cross-ply laminated composites. Compos. Sci. Technol. 34(2), 145–162 (1989).
Article CAS Google Scholar
Hashin, Z. Thermal expansion coefficients of cracked laminates. Compos. Sci. Technol. 31(4), 247–260 (1988).
Article CAS Google Scholar
Herakovich, C. T. & Hyer, M. W. Damage-induced property changes in composites subjected to cyclic thermal loading. Eng. Fract. Mech. 25(5), 779–791 (1986).
Article Google Scholar
Camahort, J. L., Rennhack, E. H. & Coons, W. C. Effects of Thermal Cycling Environment on Graphite/Epoxy Composites 37–49 (West Conshohocken, PA, ASTM International, 1976).
Google Scholar
Feltham, S. J., Yates, B. & Martin, R. J. The thermal expansion of particulate-reinforced composites. J. Mater. Sci. 17(8), 2309–2323 (1982).
Article ADS CAS Google Scholar
Zhang, J. et al. Effect of nanoparticles on interfacial properties of carbon fibre–epoxy composites. Compos. A Appl. Sci. Manuf. 55, 35–44 (2013).
Article CAS Google Scholar
Patterson, A. L. The scherrer formula for X-ray particle size determination. Phys. Rev. 56(10), 978–982 (1939).
Article ADS CAS MATH Google Scholar
Steyn-Ross, A. & Riddell, A. Standing waves in a microwave oven. Phys. Teach. 28, 474 (1990).
Article ADS Google Scholar
Kamol, S., Limsuwan, P. & Onreabroy, W. Three-dimensional standing waves in a microwave oven. Am. J. Phys. 78(5), 492–495 (2010).
Article ADS Google Scholar
Lincoln, J. An improved technique for visualizing microwave wavelengths in microwave ovens. Phys. Teach. 57(4), 271–271 (2019).
Article ADS Google Scholar
Zheng, P. et al. Grain-size effects on dielectric and piezoelectric properties of poled BaTiO3 ceramics. Acta Mater. 60(13), 5022–5030 (2012).
Article ADS CAS Google Scholar
Lei, Z. et al. An experimental analysis of residual stress measurements in porous silicon using micro-raman spectroscopy. Chin. Phys. Lett. 21, 403 (2004).
Article ADS CAS Google Scholar
Download references
The authors would like to acknowledge the grants received for this research from the UK Engineering & Physical Sciences Research Council (EPSRC), Ref. EP/R016828/1 (Self-tuning Fibre-Reinforced Polymer Adaptive Nanocomposite, STRAINcomp) and EP/R513027/1 (Study of Microstructure of Dielectric Polymer Nanocomposites subjected to Electromagnetic Field for Development of Self-toughening Lightweight Composites), and Foundation for Polish Science (FNP) under Grant Number First TEAM/2016-1/7, co-financed by the European Union under the European Regional Development Fund. We would also like to express our deepest gratitude to Prof. Vijay Kumar Thakur, Drs. Christine Kimpton, Adrianus Indrat Aria and Junfeng Chen, and Mr. Jim Hurly, Ben Hopper, Steve Pope and Andrea Giampiccolo, for their continuing support during the research. The underpinning data can be accessed at https://doi.org/10.17862/cranfield.rd.19420049.v1.
Enhanced Composites and Structures Centre, School of Aerospace, Transport and Manufacturing, Cranfield University, Cranfield, UK
Danning Li, David Ayre & Hamed Yazdani Nezhad
Centre for Engineering Photonics, School of Aerospace, Transport and Manufacturing, Cranfield University, Cranfield, UK
James Barrington & Stephen James
Faculty of Mechatronics, Warsaw University of Technology, Warsaw, Poland
Marcin Słoma
Department of Materials Engineering, Ming Chi University of Science and Technology, New Taipei, Taiwan
Meng-Fang Lin
Department of Mechanical Engineering and Aeronautics, Aeronautics and Aerospace Research Centre, City, University of London, London, UK
Hamed Yazdani Nezhad
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
D.L. designed the experimental test, conducted the characterisations, derived the theoretical calculations and conducted the experimentations. D.L. and M.L. developed the synthesis and functionalisation techniques for uniform dispersion of BaTiO3 in epoxy. They fabricated the well-dispersed nanocomposites. H.Y.N. supervised the research as the principal investigator, provided the first hypothesis, contributed to the experimental design and theoretical developments. D.L. and H.Y.N wrote the main manuscript. D.A., D.L. and H.Y.N. critically analysed the data from the theoretical and experimental approaches taken throughout the research. J.B. and S.J. developed and integrated the fibre optic sensors onto the nanocomposite specimens. M.S. contributed to the critical analysis of the experimental data and more specifically on the dielectric data, and conducted the dielectric measurements.
Correspondence to Danning Li or Hamed Yazdani Nezhad.
The authors declare no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
Reprints and Permissions
Li, D., Barrington, J., James, S. et al. Electromagnetic field controlled domain wall displacement for induced strain tailoring in BaTiO3-epoxy nanocomposite. Sci Rep 12, 7504 (2022). https://doi.org/10.1038/s41598-022-11380-9
Download citation
Received: 29 December 2021
Accepted: 22 April 2022
Published: 07 May 2022
DOI: https://doi.org/10.1038/s41598-022-11380-9
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
Functional Composite Materials (2023)